Quantitative X-Ray Diffraction Analysis of Zn-Al Based Alloys
The paper describes modification to Fm3–m (space group no. 225) lattice of aluminium based α-solid solution observed in Zn-Al alloys required to properly correlate quantitative data from X-ray diffraction analysis with results obtained from quantitative scanning electron microscopy image analysis an...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Polish Academy of Sciences
2020-05-01
|
| Series: | Archives of Metallurgy and Materials |
| Subjects: | |
| Online Access: | https://journals.pan.pl/Content/116081/PDF/AMM-2020-2-58-Kusy.pdf |
| _version_ | 1798040957333012480 |
|---|---|
| author | P. Gogola Z. Gabalcová H. Suchánek M. Babinec M. Bonek M. Kusý |
| author_facet | P. Gogola Z. Gabalcová H. Suchánek M. Babinec M. Bonek M. Kusý |
| author_sort | P. Gogola |
| collection | DOAJ |
| description | The paper describes modification to Fm3–m (space group no. 225) lattice of aluminium based α-solid solution observed in Zn-Al alloys required to properly correlate quantitative data from X-ray diffraction analysis with results obtained from quantitative scanning electron microscopy image analysis and those predicted from Zn-Al binary phase diagram. Results suggests that 14 at.% of Zn as a solute atom should be introduced in crystal lattice of aluminium to obtain correct estimation of phase quantities determined by quantitative X-ray diffraction analysis. It was shown that this modification holds for Cu mould cast as well as annealed and water-cooled samples of Zn-3wt.%. Al and Zn-5wt.% Al. |
| first_indexed | 2024-04-11T22:14:52Z |
| format | Article |
| id | doaj.art-a8dedcde40cb4a60a79ce4af4a6568d8 |
| institution | Directory Open Access Journal |
| issn | 2300-1909 |
| language | English |
| last_indexed | 2024-04-11T22:14:52Z |
| publishDate | 2020-05-01 |
| publisher | Polish Academy of Sciences |
| record_format | Article |
| series | Archives of Metallurgy and Materials |
| spelling | doaj.art-a8dedcde40cb4a60a79ce4af4a6568d82022-12-22T04:00:27ZengPolish Academy of SciencesArchives of Metallurgy and Materials2300-19092020-05-01vol. 65No 2959966https://doi.org/10.24425/amm.2020.132844Quantitative X-Ray Diffraction Analysis of Zn-Al Based AlloysP. GogolaZ. GabalcováH. SuchánekM. BabinecM. BonekM. KusýThe paper describes modification to Fm3–m (space group no. 225) lattice of aluminium based α-solid solution observed in Zn-Al alloys required to properly correlate quantitative data from X-ray diffraction analysis with results obtained from quantitative scanning electron microscopy image analysis and those predicted from Zn-Al binary phase diagram. Results suggests that 14 at.% of Zn as a solute atom should be introduced in crystal lattice of aluminium to obtain correct estimation of phase quantities determined by quantitative X-ray diffraction analysis. It was shown that this modification holds for Cu mould cast as well as annealed and water-cooled samples of Zn-3wt.%. Al and Zn-5wt.% Al.https://journals.pan.pl/Content/116081/PDF/AMM-2020-2-58-Kusy.pdfhot-dip coatingquantitative x-ray diffractionimage analysiszn-al alloy |
| spellingShingle | P. Gogola Z. Gabalcová H. Suchánek M. Babinec M. Bonek M. Kusý Quantitative X-Ray Diffraction Analysis of Zn-Al Based Alloys Archives of Metallurgy and Materials hot-dip coating quantitative x-ray diffraction image analysis zn-al alloy |
| title | Quantitative X-Ray Diffraction Analysis of Zn-Al Based Alloys |
| title_full | Quantitative X-Ray Diffraction Analysis of Zn-Al Based Alloys |
| title_fullStr | Quantitative X-Ray Diffraction Analysis of Zn-Al Based Alloys |
| title_full_unstemmed | Quantitative X-Ray Diffraction Analysis of Zn-Al Based Alloys |
| title_short | Quantitative X-Ray Diffraction Analysis of Zn-Al Based Alloys |
| title_sort | quantitative x ray diffraction analysis of zn al based alloys |
| topic | hot-dip coating quantitative x-ray diffraction image analysis zn-al alloy |
| url | https://journals.pan.pl/Content/116081/PDF/AMM-2020-2-58-Kusy.pdf |
| work_keys_str_mv | AT pgogola quantitativexraydiffractionanalysisofznalbasedalloys AT zgabalcova quantitativexraydiffractionanalysisofznalbasedalloys AT hsuchanek quantitativexraydiffractionanalysisofznalbasedalloys AT mbabinec quantitativexraydiffractionanalysisofznalbasedalloys AT mbonek quantitativexraydiffractionanalysisofznalbasedalloys AT mkusy quantitativexraydiffractionanalysisofznalbasedalloys |