Vacuum Brazing of Dissimilar Al 7075 and Al–25 Si Alloy
The vacuum brazing of dissimilar Al 7075 and Al–25 Si alloy was investigated. The brazing filler was copper foil with a thickness of 20 μm, and the brazing temperature was 560 °C held for 10 min. The average shear strength of the brazed joint of dissimilar Al 7075 and Al–25 Si alloy was 26.4 MPa. Th...
Main Authors: | Dashuang Liu, Ping Wei, Weimin Long, Wei Zhou |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-06-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/12/6/1042 |
Similar Items
-
Vacuum brazing of dissimilar Al 7075 and Al–25 Si alloy
by: Liu, Dashuang, et al.
Published: (2023) -
Contact Reactive Brazing of TC4 Alloy to Al7075 Alloy with Deposited Cu Interlayer
by: Mengjuan Yang, et al.
Published: (2021-11-01) -
Interfacial structure and strength of Al‐25Si‐4Mg‐1Cu joint brazed with Zn interlayer
by: Qiang Ma, et al.
Published: (2023-08-01) -
Effect of Brazing Fillet on the Microstructure and Mechanical Properties of Vacuum Brazing Stainless Steel Joints
by: Huixin Chen, et al.
Published: (2023-07-01) -
<i>In Situ</i> Synthesis of Al-Si-Cu Alloy During Brazing Process and Mechanical Property of Brazing Joint
by: LONG Wei-min, et al.
Published: (2016-06-01)