Microstructure formation during thermomechanical processing in Ti-17 alloy
The microstructure evolution during solution treatment at (alpha+beta) two phase region and subsequent aging process at 620 ˚C, after compressing the specimen in beta structure to different strain (0-70%) followed by cooling to room temperature has been investigated. Deformation strain hardly affect...