Structural, electrical transport and optical properties of doped La0.7Ca0.3MnO3 ceramics
In this study, we have investigated the structural, electrical transport and UV–Visible properties of polycrystalline La0.7Ca0.3−xKxMnO3 (x = 0.0, 0.05, 0.10, 0.20) ceramic samples prepared by conventional solid-state reaction. The structure characterized by X-ray diffraction shows that the samples...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2022-11-01
|
| Series: | Boletín de la Sociedad Española de Cerámica y Vidrio |
| Subjects: | |
| Online Access: | http://www.sciencedirect.com/science/article/pii/S0366317521000704 |
| _version_ | 1811201733452365824 |
|---|---|
| author | Pratik Lakhani Minal Unadkat Pankaj Solanki Jaysukh H. Markana Mukesh Ranjan Bharat Kataria |
| author_facet | Pratik Lakhani Minal Unadkat Pankaj Solanki Jaysukh H. Markana Mukesh Ranjan Bharat Kataria |
| author_sort | Pratik Lakhani |
| collection | DOAJ |
| description | In this study, we have investigated the structural, electrical transport and UV–Visible properties of polycrystalline La0.7Ca0.3−xKxMnO3 (x = 0.0, 0.05, 0.10, 0.20) ceramic samples prepared by conventional solid-state reaction. The structure characterized by X-ray diffraction shows that the samples possess orthorhombic perovskite structure belonging to Pnma space group with some impurity for higher doping level (x = 0.10, 0.20) and cell volume is enlarged with Ca2+ substitution by K1+. The surface morphology was investigated by field emission scanning electron microscope, which indicates that the samples with better crystallization having higher density. The electrical transport properties were measured by the standard four-probe method, which demonstrates that the resistivity decreases non-monotonically and the metal–insulator transition temperature (TP) shifts to higher temperature with increasing K1+ content, the electrical transport behavior for metal and insulator region was explained using Zener double exchange model and small polaron hopping model respectively. Furthermore, the progressive substitution of Ca2+ by K1+ broadens the metal–insulator transition and reduces the temperature coefficient of resistivity. Room temperature UV–Vis studies show that the optical band gap changes with the partial replacement of Ca2+ with K1+. The investigations clearly show the effect of impurity present on structural, electrical transport and UV–visible response of the prepared ceramic samples. Resumen: En este estudio, hemos investigado las propiedades estructurales, de transporte eléctrico y UV-visible de muestras cerámicas policristalinas de La0.7Ca0.3-xKxMnO3 (x = 0,0, 0,05, 0,10, 0,20) preparadas por reacción convencional en estado sólido. La estructura comprobada por difracción de rayos X muestra que las muestras poseen una estructura perovskita ortorrómbica perteneciente al grupo espacial Pnma con algunas impurezas para niveles de dopaje más altos (x = 0,10, 0,20) y el volumen de las celdas se amplía con la sustitución de Ca2+ por K1+. La morfología de la superficie se investigó mediante un microscopio electrónico de barrido de emisión de campo, que indica que las muestras con mejor cristalización tienen mayor densidad. Las propiedades de transporte eléctrico se midieron mediante el método estándar de cuatro sondas, que demuestra que la resistividad disminuye de forma no monótona y la temperatura de transición metal-aislante (TP) se desplaza a una temperatura más alta con el aumento del contenido de K1+, el comportamiento de transporte eléctrico para la región de metal y aislante se explicó utilizando el modelo de intercambio doble de Zener y el modelo de esperanza de polaron pequeño, respectivamente. Además, la sustitución progresiva de Ca2+ por K1+ amplía la transición metal-aislante y reduce el coeficiente de temperatura de la resistividad. Los estudios de UV-Vis a temperatura ambiente muestran que la brecha de banda óptica cambia con la sustitución parcial de Ca2+ por K1+. Las investigaciones muestran claramente el efecto de la impureza presente en la respuesta estructural, de transporte eléctrico y de UV-visible de las muestras cerámicas preparadas. |
| first_indexed | 2024-04-12T02:26:52Z |
| format | Article |
| id | doaj.art-ac2b26141d554d00b15fa2e1af613281 |
| institution | Directory Open Access Journal |
| issn | 0366-3175 |
| language | English |
| last_indexed | 2024-04-12T02:26:52Z |
| publishDate | 2022-11-01 |
| publisher | Elsevier |
| record_format | Article |
| series | Boletín de la Sociedad Española de Cerámica y Vidrio |
| spelling | doaj.art-ac2b26141d554d00b15fa2e1af6132812022-12-22T03:51:59ZengElsevierBoletín de la Sociedad Española de Cerámica y Vidrio0366-31752022-11-01616686696Structural, electrical transport and optical properties of doped La0.7Ca0.3MnO3 ceramicsPratik Lakhani0Minal Unadkat1Pankaj Solanki2Jaysukh H. Markana3Mukesh Ranjan4Bharat Kataria5Department of Physics, Saurashtra University, Rajkot, IndiaDepartment of Physics, Saurashtra University, Rajkot, IndiaDepartment of Physics, Saurashtra University, Rajkot, India; Department of Nanoscience and Advanced Materials, Saurashtra University, Rajkot, IndiaV.V.P. Engineering College, Rajkot, IndiaFacilitation Centre for Industrial Plasma Technologies, Gandhinagar, IndiaDepartment of Nanoscience and Advanced Materials, Saurashtra University, Rajkot, India; Corresponding author.In this study, we have investigated the structural, electrical transport and UV–Visible properties of polycrystalline La0.7Ca0.3−xKxMnO3 (x = 0.0, 0.05, 0.10, 0.20) ceramic samples prepared by conventional solid-state reaction. The structure characterized by X-ray diffraction shows that the samples possess orthorhombic perovskite structure belonging to Pnma space group with some impurity for higher doping level (x = 0.10, 0.20) and cell volume is enlarged with Ca2+ substitution by K1+. The surface morphology was investigated by field emission scanning electron microscope, which indicates that the samples with better crystallization having higher density. The electrical transport properties were measured by the standard four-probe method, which demonstrates that the resistivity decreases non-monotonically and the metal–insulator transition temperature (TP) shifts to higher temperature with increasing K1+ content, the electrical transport behavior for metal and insulator region was explained using Zener double exchange model and small polaron hopping model respectively. Furthermore, the progressive substitution of Ca2+ by K1+ broadens the metal–insulator transition and reduces the temperature coefficient of resistivity. Room temperature UV–Vis studies show that the optical band gap changes with the partial replacement of Ca2+ with K1+. The investigations clearly show the effect of impurity present on structural, electrical transport and UV–visible response of the prepared ceramic samples. Resumen: En este estudio, hemos investigado las propiedades estructurales, de transporte eléctrico y UV-visible de muestras cerámicas policristalinas de La0.7Ca0.3-xKxMnO3 (x = 0,0, 0,05, 0,10, 0,20) preparadas por reacción convencional en estado sólido. La estructura comprobada por difracción de rayos X muestra que las muestras poseen una estructura perovskita ortorrómbica perteneciente al grupo espacial Pnma con algunas impurezas para niveles de dopaje más altos (x = 0,10, 0,20) y el volumen de las celdas se amplía con la sustitución de Ca2+ por K1+. La morfología de la superficie se investigó mediante un microscopio electrónico de barrido de emisión de campo, que indica que las muestras con mejor cristalización tienen mayor densidad. Las propiedades de transporte eléctrico se midieron mediante el método estándar de cuatro sondas, que demuestra que la resistividad disminuye de forma no monótona y la temperatura de transición metal-aislante (TP) se desplaza a una temperatura más alta con el aumento del contenido de K1+, el comportamiento de transporte eléctrico para la región de metal y aislante se explicó utilizando el modelo de intercambio doble de Zener y el modelo de esperanza de polaron pequeño, respectivamente. Además, la sustitución progresiva de Ca2+ por K1+ amplía la transición metal-aislante y reduce el coeficiente de temperatura de la resistividad. Los estudios de UV-Vis a temperatura ambiente muestran que la brecha de banda óptica cambia con la sustitución parcial de Ca2+ por K1+. Las investigaciones muestran claramente el efecto de la impureza presente en la respuesta estructural, de transporte eléctrico y de UV-visible de las muestras cerámicas preparadas.http://www.sciencedirect.com/science/article/pii/S0366317521000704CerámicaDifracción de rayos XAncho de banda electrónicoPropiedades de transporte eléctricoEstudios UV-Vis |
| spellingShingle | Pratik Lakhani Minal Unadkat Pankaj Solanki Jaysukh H. Markana Mukesh Ranjan Bharat Kataria Structural, electrical transport and optical properties of doped La0.7Ca0.3MnO3 ceramics Boletín de la Sociedad Española de Cerámica y Vidrio Cerámica Difracción de rayos X Ancho de banda electrónico Propiedades de transporte eléctrico Estudios UV-Vis |
| title | Structural, electrical transport and optical properties of doped La0.7Ca0.3MnO3 ceramics |
| title_full | Structural, electrical transport and optical properties of doped La0.7Ca0.3MnO3 ceramics |
| title_fullStr | Structural, electrical transport and optical properties of doped La0.7Ca0.3MnO3 ceramics |
| title_full_unstemmed | Structural, electrical transport and optical properties of doped La0.7Ca0.3MnO3 ceramics |
| title_short | Structural, electrical transport and optical properties of doped La0.7Ca0.3MnO3 ceramics |
| title_sort | structural electrical transport and optical properties of doped la0 7ca0 3mno3 ceramics |
| topic | Cerámica Difracción de rayos X Ancho de banda electrónico Propiedades de transporte eléctrico Estudios UV-Vis |
| url | http://www.sciencedirect.com/science/article/pii/S0366317521000704 |
| work_keys_str_mv | AT pratiklakhani structuralelectricaltransportandopticalpropertiesofdopedla07ca03mno3ceramics AT minalunadkat structuralelectricaltransportandopticalpropertiesofdopedla07ca03mno3ceramics AT pankajsolanki structuralelectricaltransportandopticalpropertiesofdopedla07ca03mno3ceramics AT jaysukhhmarkana structuralelectricaltransportandopticalpropertiesofdopedla07ca03mno3ceramics AT mukeshranjan structuralelectricaltransportandopticalpropertiesofdopedla07ca03mno3ceramics AT bharatkataria structuralelectricaltransportandopticalpropertiesofdopedla07ca03mno3ceramics |