| Summary: | In this investigation, pure aluminum (Al) powders were cryomilled with and without magnesium dopants to study (a) the effect of cryomilling time on the crystallite size and (b) the effect of magnesium dopant on Al to achieve grain boundary stability. The cryomilling process was carried out using liquid nitrogen for different durations. The characterization of the cryomilled powders was carried out using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction (XRD) to understand the particle morphology, crystallite size, and elemental composition. The results demonstrated that the size of the crystallites in both Al and Mg-doped Al powders reduces as the cryomilling duration increases. The results also indicated that the preferential segregation of Mg dopant at the grain boundaries of Al provides stability to the cryomilled powders at elevated temperatures. This article discusses the mechanism for the changes in crystallite size and the effect of the Mg dopant on the grain boundary stability in Al powders.
|
|---|