| Summary: | Additive manufacturing technologies based on metal melting use materials mainly in powder or wire form. This study focuses on developing a metal 3D printing process based on cold metal transfer (CMT) welding technology, in order to achieve enhanced productivity. Aluminium alloy test specimens have been fabricated using a special 3D printing technology. The probes were investigated to find correlation between the welding parameters and geometric quality. Geometric measurements and tensile strength experiments were performed to determine the appropriate welding parameters for reliable printing. The tensile strength of the product does not differ significantly from the raw material. Above 60 mm height, the wall thickness is relatively constant due to the thermal balance of the welding environment. The results suggest that there might be a connection between the welding parameters and the printing accuracy. It is demonstrated that the deviation of ideal geometry will be the smallest at the maximum reliable welding torch movement speed, while printing larger specimens. As a conclusion, it can be stated that CMT-based additive manufacturing can be a reliable, cost-effective and rapid 3D printing technology with enhanced productivity, but without significant decrease in mechanical stability.
|
|---|