Ultrasonic fatigue tests on maraging 300 steel: Under solution annealed, after aging heat treatment and under pre-corrosion attack
Ultrasonic fatigue tests were carried out under continuous cycling on the maraging 300 steel for the following conditions: (A) solution annealed (as received from supplier), (B) after aging heat treatment of 490 °C for 6 h, (C) after pre-corrosion attack, and (D) specimens loaded at 293 MPa at room...
Main Authors: | Julio A. Ruiz Vilchez, Gonzalo M. Domínguez Almaraz, Aymeric E. Domínguez |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2024-02-01
|
Series: | Forces in Mechanics |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S2666359723000884 |
Similar Items
-
Influence of Deposition Plane Angle and Saline Corrosion on Fatigue Crack Growth in Maraging Steel Components Produced by Laser Powder Bed Fusion
by: Rui F. Fernandes, et al.
Published: (2022-03-01) -
Strengthening mechanism in fatigue of maraging steel at elevated temperature
by: Norio KAWAGOISHI, et al.
Published: (2020-10-01) -
Heterogeneous effect of aging temperature on the fatigue life of additively manufactured thin-walled 18Ni300 maraging steel tubular specimen
by: Aleksander Karolczuk, et al.
Published: (2024-01-01) -
Three-Dimensional Surface Crack Growth of Maraging Steel Spherical Pressure Shell
by: Yongmei Zhu, et al.
Published: (2021-11-01) -
Crack initiation and propagation on the polymeric material ABS (Acrylonitrile Butadiene Styrene), under ultrasonic fatigue testing
by: G. M. Domínguez Almaraz, et al.
Published: (2015-10-01)