Influence of Surface Roughness on the High Temperature /High Strain Low Cycle Fatigue Behavior of Nickel-Based Superalloy Rene®80
Since fatigue cracks nucleate and initiate generally at the surface of the rotary components such as blades and discs, the surface condition is the most important factor affecting the fatigue life. Surface scratches are suitable sites for stress concentrations and therefore the nucleation stage of f...
Main Author: | Mohammad Mehdi Barjesteh |
---|---|
Format: | Article |
Language: | English |
Published: |
Polish Academy of Sciences
2023-06-01
|
Series: | Archives of Metallurgy and Materials |
Subjects: | |
Online Access: | https://journals.pan.pl/Content/127275/PDF/AMM-2023-2-13-Barjesteh.pdf |
Similar Items
-
Effects of check corrosion on high cycle fatigue properties of nickel-base single crystal superalloy
by: DONG Jian-min, et al.
Published: (2020-01-01) -
ISOTHERMAL AND THERMOMECHANICAL FATIGUE OF A NICKEL-BASE SUPERALLOY
by: Carlos Carvalho Engler-Pinto Júnior, et al.
Published: (2014-06-01) -
Orientation Dependence of High Cycle Fatigue Behavior of a <111> Oriented Single-Crystal Nickel-Based Superalloy
by: Bin Hu, et al.
Published: (2021-08-01) -
Cracking Behavior of René 104 Nickel-Based Superalloy Prepared by Selective Laser Melting Using Different Scanning Strategies
by: Kai Peng, et al.
Published: (2020-05-01) -
LOW CYCLE FATIGUE LIFE PREDICTION METHOD FOR SINGLE CRYSTAL NICKEL-BASE SUPERALLOYS AT HIGH TEMPERATURE
by: CHEN Hong, et al.
Published: (2015-01-01)