Internal friction at crack tip of soda-lime silicate glass
Oxide glasses exhibit slow crack growth (SCG) behavior in the presence of water vapor. Oxide glasses are generally considered to be perfectly brittle materials exhibiting no plastic deformation at room temperature. The SCG behavior is generally classified into three regions, region I, region II and...