Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM
The article presents the results of a study of the wear resistance of sintered specimens from electroerosive powder of steel X13, obtained in butyl alcohol. The friction coefficient was 0.950, the width of the wear groove was 455.9 µm, the depth of the wear groove was 6 µm, the wear factor of the sa...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2021-01-01
|
| Series: | MATEC Web of Conferences |
| Online Access: | https://www.matec-conferences.org/articles/matecconf/pdf/2021/15/matecconf_icmtmte2021_02018.pdf |
| _version_ | 1818407579724808192 |
|---|---|
| author | Ageev E.V. Khardikov S.V. Loktionova O.G. Kolmykov V.I. |
| author_facet | Ageev E.V. Khardikov S.V. Loktionova O.G. Kolmykov V.I. |
| author_sort | Ageev E.V. |
| collection | DOAJ |
| description | The article presents the results of a study of the wear resistance of sintered specimens from electroerosive powder of steel X13, obtained in butyl alcohol. The friction coefficient was 0.950, the width of the wear groove was 455.9 µm, the depth of the wear groove was 6 µm, the wear factor of the sample was 1.676x10-6 mm3 N-1m-1. |
| first_indexed | 2024-12-14T09:30:05Z |
| format | Article |
| id | doaj.art-b748b3edcee44a469acd68b72cbaafa6 |
| institution | Directory Open Access Journal |
| issn | 2261-236X |
| language | English |
| last_indexed | 2024-12-14T09:30:05Z |
| publishDate | 2021-01-01 |
| publisher | EDP Sciences |
| record_format | Article |
| series | MATEC Web of Conferences |
| spelling | doaj.art-b748b3edcee44a469acd68b72cbaafa62022-12-21T23:08:05ZengEDP SciencesMATEC Web of Conferences2261-236X2021-01-013460201810.1051/matecconf/202134602018matecconf_icmtmte2021_02018Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDMAgeev E.V.0Khardikov S.V.1Loktionova O.G.2Kolmykov V.I.3Southwest State UniversitySouthwest State UniversitySouthwest State UniversitySouthwest State UniversityThe article presents the results of a study of the wear resistance of sintered specimens from electroerosive powder of steel X13, obtained in butyl alcohol. The friction coefficient was 0.950, the width of the wear groove was 455.9 µm, the depth of the wear groove was 6 µm, the wear factor of the sample was 1.676x10-6 mm3 N-1m-1.https://www.matec-conferences.org/articles/matecconf/pdf/2021/15/matecconf_icmtmte2021_02018.pdf |
| spellingShingle | Ageev E.V. Khardikov S.V. Loktionova O.G. Kolmykov V.I. Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM MATEC Web of Conferences |
| title | Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_full | Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_fullStr | Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_full_unstemmed | Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_short | Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_sort | analysis of wear resisting properties of a sintered sample obtained from steel x13 machined using edm |
| url | https://www.matec-conferences.org/articles/matecconf/pdf/2021/15/matecconf_icmtmte2021_02018.pdf |
| work_keys_str_mv | AT ageevev analysisofwearresistingpropertiesofasinteredsampleobtainedfromsteelx13machinedusingedm AT khardikovsv analysisofwearresistingpropertiesofasinteredsampleobtainedfromsteelx13machinedusingedm AT loktionovaog analysisofwearresistingpropertiesofasinteredsampleobtainedfromsteelx13machinedusingedm AT kolmykovvi analysisofwearresistingpropertiesofasinteredsampleobtainedfromsteelx13machinedusingedm |