Fracture Behavior of a Unidirectional Carbon Fiber-Reinforced Plastic under Biaxial Tensile Loads
In order to clarify the fracture behavior of a unidirectional CFRP under proportional loading along the fiber (0°) and fiber vertical (90°) directions, a biaxial tensile test was carried out using a cruciform specimen with two symmetric flat indentations in the thickness direction. Three fracture mo...
Main Authors: | Kosuke Sanai, Sho Nakasaki, Mikiyasu Hashimoto, Arnaud Macadre, Koichi Goda |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2024-03-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/17/6/1387 |
Similar Items
-
The characterization of unidirectional and woven water hyacinth fiber reinforced with epoxy resin composites
by: S. Sulardjaka, et al.
Published: (2022-09-01) -
RESEARCH ON STIFFNESS REDUCTION OF UNIDIRECTIONAL LAMINATES UNDER STATIC TENSILE LOADS
by: WANG Le, et al.
Published: (2017-01-01) -
Experimental Study of Mechanical Properties of Unidirectional Woven Carbon Fiber and Fiber Glass - Epoxy Composites
by: Naznaz Jalal Awla, et al.
Published: (2023-02-01) -
Mechanical and Hygroscopic Characteristics of Unidirectional Jute/Glass and Jute/Carbon Hybrid Laminates
by: André Flores, et al.
Published: (2023-04-01) -
Strength analysis of marine biaxial warp-knitted glass fabrics as composite laminations for ship material
by: Ma’ruf Buana, et al.
Published: (2023-08-01)