Improving the Reactivity of Sugarcane Bagasse Kraft Lignin by a Combination of Fractionation and Phenolation for Phenol–Formaldehyde Adhesive Applications
The low reactivity of lignin hinders its application as a phenol substitute in phenol–formaldehyde (PF) resin. Therefore, the combination of fractionation and phenolation was adopted to enhance the reactivity of lignin for preparing a phenol–formaldehyde resin adhesive. Sugarcane bagasse kraft ligni...
Main Authors: | Bin Luo, Zhuan Jia, Hongrui Jiang, Shuangfei Wang, Douyong Min |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-08-01
|
Series: | Polymers |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4360/12/8/1825 |
Similar Items
-
Paper-Based Laminates Impregnated with a Hybrid Lignin-Phenol-Formaldehyde Resin
by: Miroslav Němec, et al.
Published: (2023-03-01) -
Evaluation and Optimization of Kraft Delignification and Single Stage Hydrogen Peroxide Bleaching for Ethiopian Sugarcane Bagasse
by: Medhanit Mamaye, et al.
Published: (2022-04-01) -
Bond quality of poplar plywood reinforced with hemp fibers and lignin-phenolic adhesives
by: Ramesh Karri, et al.
Published: (2022-10-01) -
A Comparison among Lignin Modification Methods on the Properties of Lignin–Phenol–Formaldehyde Resin as Wood Adhesive
by: Hamed Younesi-Kordkheili, et al.
Published: (2021-10-01) -
Studies on the Removal of Phenol and Nitrophenols from Water by Activated Carbon Developed from Demineralized Kraft Lignin
by: Monika Chaudhary, et al.
Published: (2022-10-01)