Multigraphene Prepared by One-Pot Pyrolysis of Diatomite/Polypropylene Composites
Multigraphene was prepared via a one-pot pyrolysis method using polypropylene (PP) as the carbon source and diatomite (DM) as the catalyst. The obtained graphene had 4–6 layers and a D/G intensity ratio of 0.70 and a 2D/G intensity ratio of 0.72, indicating a high degree of graphitization. When the...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2022-03-01
|
| Series: | Applied Sciences |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2076-3417/12/5/2687 |
| Summary: | Multigraphene was prepared via a one-pot pyrolysis method using polypropylene (PP) as the carbon source and diatomite (DM) as the catalyst. The obtained graphene had 4–6 layers and a D/G intensity ratio of 0.70 and a 2D/G intensity ratio of 0.72, indicating a high degree of graphitization. When the pyrolysis temperature was higher than 850 °C under argon, the graphene yield was greatly dependent on the DM content. The highest graphene yield of 25.86% was obtained by pyrolysis of PP with 30 wt.% DM at the temperature of 1000 °C. A catalytic effect of DM and infusible cross-linking structure formation were proposed to explain the possible mechanism of graphene growth during the pyrolysis of the DM/PP composites. |
|---|---|
| ISSN: | 2076-3417 |