Isothermal Oxidation of Aluminized Coatings on High-Entropy Alloys
The isothermal oxidation resistance of Al0.2Co1.5CrFeNi1.5Ti0.3 high-entropy alloy is analyzed and the microstructural evolution of the oxide layer is studied. The limited aluminum, about 3.6 at %, leads to the non-continuous alumina. The present alloy is insufficient for severe circumstances only d...
Main Authors: | Che-Wei Tsai, Kuen-Cheng Sung, Kzauki Kasai, Hideyuki Murakami |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2016-10-01
|
Series: | Entropy |
Subjects: | |
Online Access: | http://www.mdpi.com/1099-4300/18/10/376 |
Similar Items
-
Wear and Corrosion Resistance of Plasma Electrolytic Oxidation Coatings on 6061 Al Alloy in Electrolytes with Aluminate and Phosphate
by: Zhenjun Peng, et al.
Published: (2021-07-01) -
Calcium Aluminate Cement Hydration Model
by: Matusinović, T., et al.
Published: (2011-01-01) -
Recent Developments in Lanthanide-Doped Alkaline Earth Aluminate Phosphors with Enhanced and Long-Persistent Luminescence
by: Doory Kim
Published: (2021-03-01) -
Effect of Slurry Thickness on the Quality of Aluminized Coatings
by: Zhuoyue Li, et al.
Published: (2022-09-01) -
High-temperature Corrosion Resistance of Composite Coating Prepared by Micro-arc Oxidation Combined with Pack Cementation Aluminizing
by: HUANG Zu-jiang, et al.
Published: (2018-01-01)