Suppression of liquation cracking susceptibility via pre-weld heat treatment for manufacturing of CM247LC superalloy turbine blade welds
In this study, the weldability of as-cast CM247LC superalloy was metallurgically evaluated for turbine blade applications in terms of its hot cracking behavior and susceptibility. For this purpose, a real blade was manufactured using a directional solidification casting process, and gas tungsten arc...