The Microstructure and Mechanical Properties of Cu-20Ni-20Mn Alloy Fabricated by a Compact Preparation Process
A novel compact preparation process has been developed to produce a Cu-20Ni-20Mn alloy. This process involves heating-cooling combined mould (HCCM) continuous casting, a solution treatment at 800 °C, rolling at room temperature and a final ageing step at 450 °C. This process eliminates two hot defor...
Main Authors: | Rui Wang, Yilei Fu, Guoliang Xie, Zifan Hao, Shuai Zhang, Xinhua Liu |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-11-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/10/11/1528 |
Similar Items
-
Hot deformation behaviour and optimization of process parameters for an as-cast Cu–20Ni–20Mn alloy
by: Jing Xu, et al.
Published: (2023-09-01) -
Martensitic Transformation and Magnetic-Field-Induced Strain in High-Entropy Magnetic Memory Alloy Ni<sub>20</sub>Mn<sub>20</sub>Ga<sub>20</sub>Gd<sub>20</sub>Co<sub>20</sub> by Hot-Magnetic Drawing
by: Jia Ju, et al.
Published: (2022-04-01) -
Highly oriented microtube arrays of decagonal quasicrystal approximants in Al20Si20Mn20Fe20Ga20 high-entropy alloy
by: Tiantian Zhang, et al.
Published: (2023-08-01) -
Study on aging strengthening and nano precipitates of Cu–Ni–Mn–Fe alloy
by: Juntao Zou, et al.
Published: (2020-01-01) -
Microstructure evolution and aging hardening in a Cu-25Ni-25Mn alloy
by: Kang Ding, et al.
Published: (2021-01-01)