“Nano in Nano”—Incorporation of ZnO Nanoparticles into Cellulose Acetate–Poly(Ethylene Oxide) Composite Nanofibers Using Solution Blow Spinning
In this work, the preparation and characterization of composites from cellulose acetate (CA)–poly(ethylene oxide) (PEO) nanofibers (NFs) with incorporated zinc oxide nanoparticles (ZnO-NPs) using solution blow spinning (SBS) is reported. CA–PEO nanofibers were produced by spinning solution that cont...
Main Authors: | Caroline Voorhis, Javier González-Benito, Ana Kramar |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2024-01-01
|
Series: | Polymers |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4360/16/3/341 |
Similar Items
-
Solution Blow Spinning to Prepare Preferred Oriented Poly(ethylene oxide) Submicrometric Fibers
by: Javier González-Benito, et al.
Published: (2023-09-01) -
Preparation of cellulose acetate film with dual hydrophobic-hydrophilic properties using solution blow spinning
by: Ana Kramar, et al.
Published: (2023-03-01) -
Chitosan-Enriched Solution Blow Spun Poly(Ethylene Oxide) Nanofibers with Poly(Dimethylsiloxane) Hydrophobic Outer Layer for Skin Healing and Regeneration
by: Emilia Szymańska, et al.
Published: (2022-05-01) -
Active Cellulose Acetate/Chitosan Composite Films Prepared Using Solution Blow Spinning: Structure and Electrokinetic Properties
by: Ana Kramar, et al.
Published: (2023-08-01) -
Cellulose-Based Nanofibers Processing Techniques and Methods Based on Bottom-Up Approach—A Review
by: Ana Kramar, et al.
Published: (2022-01-01)