Aluminum Filler Content Effect on the Dynamic Behavior of Sandwich Panel Subjectedt Impact Load
Experimental investigations had been done in this work to demonstrate the effect of aluminum filler contents on the dynamic behavior of (30%) weight fraction glass-polyester sandwich panel under low velocity impact. The composite sandwich panels are manufactured using the honeycomb core and laminate...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Unviversity of Technology- Iraq
2013-09-01
|
| Series: | Engineering and Technology Journal |
| Subjects: | |
| Online Access: | https://etj.uotechnology.edu.iq/article_83257_3c5d83b3b2d4e2af4f9412159cfa7370.pdf |
| Summary: | Experimental investigations had been done in this work to demonstrate the effect of aluminum filler contents on the dynamic behavior of (30%) weight fraction glass-polyester sandwich panel under low velocity impact. The composite sandwich panels are manufactured using the honeycomb core and laminated composite face sheets. The wet hand layup technique is used. The mechanical properties were tested based on ASTM D- 638. The panel is fixed from three sides and the other is free. The impact load is applied. The dynamic response of the plate is measured using vibration data collector (TVC 200). The panel is supported also on a rigid foundation. The steel impactor of 15 kg weight dropped from 2 m height. The deformation is measured using vernier caliper. The results showed that the mechanical properties are improved when the aluminum filler content increased up to 5% and then decreased after that. The dynamic behaviors have the same but differ in magnitude. The minimum deflection and deformation takes at 5% filler content for both face and core. At 5% filler content the deflection and deformation decreased by 20% and 56% respectively less than the unfilled panel. The effects of using different faces with the same core have a little variation. |
|---|---|
| ISSN: | 1681-6900 2412-0758 |