The Effect of the β-Al<sub>5</sub>FeSi Phases on Microstructure, Mechanical and Fatigue Properties in A356.0 Cast Alloys with Higher Fe Content without Additional Alloying of Mn

The Effect of the β-Al<sub>5</sub>FeSi Phases on Microstructure, Mechanical and Fatigue Properties in A356.0 Cast Alloys with Higher Fe Content without Additional Alloying of Mn

Secondary-cast aluminum alloys have increasing industrial applications. Their biggest deficiency is their impurity content, especially Fe, which has low solubility in Al and almost all the content creates intermetallic phases. This work examines the effect of higher Fe content on the microstructure...

Full description

Bibliographic Details
Main Authors: Lenka Kuchariková, Denisa Medvecká, Eva Tillová, Juraj Belan, Michaela Kritikos, Mária Chalupová, Milan Uhríčik
Format: Article
Language:English
Published: MDPI AG 2021-04-01
Series:Materials
Subjects:
β-Al<sub>5</sub>FeSi intermetallic phases
higher content of Fe
dismissing Mn addition
properties of aluminum alloys with higher Fe content
Online Access:https://www.mdpi.com/1996-1944/14/8/1943

Similar Items

Similar Items