Microstructure and wettability of the micro-laminated Ti6Al4V/304 stainless steel composite fabricated by diffusion bonding
Laminated composites have been extensively researched due to their excellent mechanical properties, but their application in superwetting fields has been rarely reported. In this work, the surfaces with extreme wettability were prepared based on laminated composites. The Ti6Al4V/304 stainless steel...
Main Authors: | , , , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2023-11-01
|
Series: | Journal of Materials Research and Technology |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S2238785423026686 |
_version_ | 1797301546060349440 |
---|---|
author | Dejun Gao Chun Li Chenghao Zhang Bo Yang Tong Lin Lei Chen Xiaoqing Si Junlei Qi Jian Cao |
author_facet | Dejun Gao Chun Li Chenghao Zhang Bo Yang Tong Lin Lei Chen Xiaoqing Si Junlei Qi Jian Cao |
author_sort | Dejun Gao |
collection | DOAJ |
description | Laminated composites have been extensively researched due to their excellent mechanical properties, but their application in superwetting fields has been rarely reported. In this work, the surfaces with extreme wettability were prepared based on laminated composites. The Ti6Al4V/304 stainless steel (304 SS) micro-laminated composites were fabricated by diffusion bonding the Ti6Al4V foils and 304 SS foils with the thickness of 10–50 μm in vacuum. The typical interfacial microstructure and the effect of diffusion temperature on the microstructure were investigated. The bonded interface of joints is mainly composed of β-Ti, Ti2Ni, FeTi, Fe2Ti, Fe–Cr from the Ti6Al4V side to the 304 SS. The effect of diffusion temperature on the microstructure was researched. Based on the prepared Ti6Al4V/304 SS micro-laminated composites, an array structure with micro grooves was fabricated through the simple chemical etching. The 304 SS foils were etched to form grooves, while Ti6Al4V foils still remained as bulges. Due to surface modification and rough morphology, the etched surfaces exhibited the excellent hydrophobicity. Increasing the width and depth of grooves and decreasing the width of bulges led to the higher water contact angles and improved hydrophobicity. The highest water contact angles of 148.3° has been achieved under the conditions of grooves with a width of 50 μm, a depth of 60 μm, and the bulges with a width of 10 μm. The surfaces exhibited nearly superhydrophobicity and performed self-cleaning property. The processing method of this work could expand the application of laminated composite in extreme wettability fields. |
first_indexed | 2024-03-07T23:23:12Z |
format | Article |
id | doaj.art-c1540333437c49c48e7b12a046235036 |
institution | Directory Open Access Journal |
issn | 2238-7854 |
language | English |
last_indexed | 2024-03-07T23:23:12Z |
publishDate | 2023-11-01 |
publisher | Elsevier |
record_format | Article |
series | Journal of Materials Research and Technology |
spelling | doaj.art-c1540333437c49c48e7b12a0462350362024-02-21T05:26:51ZengElsevierJournal of Materials Research and Technology2238-78542023-11-012737883796Microstructure and wettability of the micro-laminated Ti6Al4V/304 stainless steel composite fabricated by diffusion bondingDejun Gao0Chun Li1Chenghao Zhang2Bo Yang3Tong Lin4Lei Chen5Xiaoqing Si6Junlei Qi7Jian Cao8State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaCorresponding author.; State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaState Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaState Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaState Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaState Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaState Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaState Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaCorresponding author.; State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin, 150001, ChinaLaminated composites have been extensively researched due to their excellent mechanical properties, but their application in superwetting fields has been rarely reported. In this work, the surfaces with extreme wettability were prepared based on laminated composites. The Ti6Al4V/304 stainless steel (304 SS) micro-laminated composites were fabricated by diffusion bonding the Ti6Al4V foils and 304 SS foils with the thickness of 10–50 μm in vacuum. The typical interfacial microstructure and the effect of diffusion temperature on the microstructure were investigated. The bonded interface of joints is mainly composed of β-Ti, Ti2Ni, FeTi, Fe2Ti, Fe–Cr from the Ti6Al4V side to the 304 SS. The effect of diffusion temperature on the microstructure was researched. Based on the prepared Ti6Al4V/304 SS micro-laminated composites, an array structure with micro grooves was fabricated through the simple chemical etching. The 304 SS foils were etched to form grooves, while Ti6Al4V foils still remained as bulges. Due to surface modification and rough morphology, the etched surfaces exhibited the excellent hydrophobicity. Increasing the width and depth of grooves and decreasing the width of bulges led to the higher water contact angles and improved hydrophobicity. The highest water contact angles of 148.3° has been achieved under the conditions of grooves with a width of 50 μm, a depth of 60 μm, and the bulges with a width of 10 μm. The surfaces exhibited nearly superhydrophobicity and performed self-cleaning property. The processing method of this work could expand the application of laminated composite in extreme wettability fields.http://www.sciencedirect.com/science/article/pii/S2238785423026686Micro-laminated compositeDiffusion bondingTi6Al4V304 stainless steelWettability |
spellingShingle | Dejun Gao Chun Li Chenghao Zhang Bo Yang Tong Lin Lei Chen Xiaoqing Si Junlei Qi Jian Cao Microstructure and wettability of the micro-laminated Ti6Al4V/304 stainless steel composite fabricated by diffusion bonding Journal of Materials Research and Technology Micro-laminated composite Diffusion bonding Ti6Al4V 304 stainless steel Wettability |
title | Microstructure and wettability of the micro-laminated Ti6Al4V/304 stainless steel composite fabricated by diffusion bonding |
title_full | Microstructure and wettability of the micro-laminated Ti6Al4V/304 stainless steel composite fabricated by diffusion bonding |
title_fullStr | Microstructure and wettability of the micro-laminated Ti6Al4V/304 stainless steel composite fabricated by diffusion bonding |
title_full_unstemmed | Microstructure and wettability of the micro-laminated Ti6Al4V/304 stainless steel composite fabricated by diffusion bonding |
title_short | Microstructure and wettability of the micro-laminated Ti6Al4V/304 stainless steel composite fabricated by diffusion bonding |
title_sort | microstructure and wettability of the micro laminated ti6al4v 304 stainless steel composite fabricated by diffusion bonding |
topic | Micro-laminated composite Diffusion bonding Ti6Al4V 304 stainless steel Wettability |
url | http://www.sciencedirect.com/science/article/pii/S2238785423026686 |
work_keys_str_mv | AT dejungao microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding AT chunli microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding AT chenghaozhang microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding AT boyang microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding AT tonglin microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding AT leichen microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding AT xiaoqingsi microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding AT junleiqi microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding AT jiancao microstructureandwettabilityofthemicrolaminatedti6al4v304stainlesssteelcompositefabricatedbydiffusionbonding |