Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and SiC
This work focuses on the effect of electrodeposition of nickel on corrosion behavior of mild steel substrate with ultra-fine Al2O3 and SiC using electroplating technology. The experimental results exhibited the substrate microstructure was sensitive to both current density and temperature. Grain g...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | Arabic |
| Published: |
Mustansiriyah University/College of Engineering
2014-11-01
|
| Series: | Journal of Engineering and Sustainable Development |
| Subjects: | |
| Online Access: | https://jeasd.uomustansiriyah.edu.iq/index.php/jeasd/article/view/933 |
| _version_ | 1828135008364134400 |
|---|---|
| author | Nirvana Abbas AbdAlameer Shayma Hameed Mohammad Thaer Abdalwahab Shihab |
| author_facet | Nirvana Abbas AbdAlameer Shayma Hameed Mohammad Thaer Abdalwahab Shihab |
| author_sort | Nirvana Abbas AbdAlameer |
| collection | DOAJ |
| description |
This work focuses on the effect of electrodeposition of nickel on corrosion behavior of mild steel substrate with ultra-fine Al2O3 and SiC using electroplating technology. The experimental results exhibited the substrate microstructure was sensitive to both current density and temperature. Grain growth was increased with increasing each current density and temperature and thereafter decreased. Optimal values were 0.2A/cm2 and 45°C, respectively. The concentration of each Al2O3 and SiC were essential to electro-deposition, it was found at 4gm/l after the traditional weight loss technique was performed, it was found that the corrosion rate of Ni and Ni- Al2O3 was deceased with exposure time in 3.5% NaCl solution whereas Ni-SiC exhibited higher corrosion rate. the addition of Al2O3 inhibited corrosion in acid solution.
|
| first_indexed | 2024-04-11T17:41:26Z |
| format | Article |
| id | doaj.art-c3aa212d7fc34c16a406dfb3c6358e74 |
| institution | Directory Open Access Journal |
| issn | 2520-0917 2520-0925 |
| language | Arabic |
| last_indexed | 2024-04-11T17:41:26Z |
| publishDate | 2014-11-01 |
| publisher | Mustansiriyah University/College of Engineering |
| record_format | Article |
| series | Journal of Engineering and Sustainable Development |
| spelling | doaj.art-c3aa212d7fc34c16a406dfb3c6358e742022-12-22T04:11:28ZaraMustansiriyah University/College of EngineeringJournal of Engineering and Sustainable Development2520-09172520-09252014-11-01186Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and SiCNirvana Abbas AbdAlameer0Shayma Hameed Mohammad1Thaer Abdalwahab Shihab2Chemical Engineering Department, Technical Engineering College, Baghdad, IraqMaterials Engineering Techniques, Technical Engineering College, Baghdad, IraqDies and Tools Engineering Techniques, Technical Engineering College, Baghdad, Iraq This work focuses on the effect of electrodeposition of nickel on corrosion behavior of mild steel substrate with ultra-fine Al2O3 and SiC using electroplating technology. The experimental results exhibited the substrate microstructure was sensitive to both current density and temperature. Grain growth was increased with increasing each current density and temperature and thereafter decreased. Optimal values were 0.2A/cm2 and 45°C, respectively. The concentration of each Al2O3 and SiC were essential to electro-deposition, it was found at 4gm/l after the traditional weight loss technique was performed, it was found that the corrosion rate of Ni and Ni- Al2O3 was deceased with exposure time in 3.5% NaCl solution whereas Ni-SiC exhibited higher corrosion rate. the addition of Al2O3 inhibited corrosion in acid solution. https://jeasd.uomustansiriyah.edu.iq/index.php/jeasd/article/view/933electroplating nickelSiCAl2O3 |
| spellingShingle | Nirvana Abbas AbdAlameer Shayma Hameed Mohammad Thaer Abdalwahab Shihab Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and SiC Journal of Engineering and Sustainable Development electroplating nickel SiC Al2O3 |
| title | Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and SiC |
| title_full | Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and SiC |
| title_fullStr | Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and SiC |
| title_full_unstemmed | Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and SiC |
| title_short | Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and SiC |
| title_sort | studying the effect of ni electroplating on corrosion behavior in presence ultra fine al2o3 and sic |
| topic | electroplating nickel SiC Al2O3 |
| url | https://jeasd.uomustansiriyah.edu.iq/index.php/jeasd/article/view/933 |
| work_keys_str_mv | AT nirvanaabbasabdalameer studyingtheeffectofnielectroplatingoncorrosionbehaviorinpresenceultrafineal2o3andsic AT shaymahameedmohammad studyingtheeffectofnielectroplatingoncorrosionbehaviorinpresenceultrafineal2o3andsic AT thaerabdalwahabshihab studyingtheeffectofnielectroplatingoncorrosionbehaviorinpresenceultrafineal2o3andsic |