Preparation of titanium carbide powder from ilmenite concentrate
A new process of producing titanium carbide powder from ilmenite concentrate was put forward. The ilmenite concentrate was reduced by graphite powder at 1500ºC for 6 hours, with the reduction products of TiC, Fe and MgO. The porous reduction products were agitation leached in ferric chlorid...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Association of the Chemical Engineers of Serbia
2017-01-01
|
| Series: | Chemical Industry and Chemical Engineering Quarterly |
| Subjects: | |
| Online Access: | http://www.doiserbia.nb.rs/img/doi/1451-9372/2017/1451-93721600007G.pdf |
| _version_ | 1818652110889156608 |
|---|---|
| author | Gou Hai-Peng Zhang Guo-Hua Kuo-Chih Chou |
| author_facet | Gou Hai-Peng Zhang Guo-Hua Kuo-Chih Chou |
| author_sort | Gou Hai-Peng |
| collection | DOAJ |
| description | A new process of producing titanium carbide powder from ilmenite concentrate
was put forward. The ilmenite concentrate was reduced by graphite powder at
1500ºC for 6 hours, with the reduction products of TiC, Fe and MgO. The porous
reduction products were agitation leached in ferric chloride solution at
25ºC for 60 minutes. After the filtration, TiC powder accompanied by little
MgAl2O4 and Mg2SiO4 were obtained. Finally, the element Fe was recycled from
the filtrate in the form of β-FeOOH after blowing air for 3 hours at 80ºC. The
size of rod-like β-FeOOH particle was less than 1µm. |
| first_indexed | 2024-12-17T02:16:48Z |
| format | Article |
| id | doaj.art-c6ad21be60d348a5b7e4269e894df4db |
| institution | Directory Open Access Journal |
| issn | 1451-9372 2217-7434 |
| language | English |
| last_indexed | 2024-12-17T02:16:48Z |
| publishDate | 2017-01-01 |
| publisher | Association of the Chemical Engineers of Serbia |
| record_format | Article |
| series | Chemical Industry and Chemical Engineering Quarterly |
| spelling | doaj.art-c6ad21be60d348a5b7e4269e894df4db2022-12-21T22:07:23ZengAssociation of the Chemical Engineers of SerbiaChemical Industry and Chemical Engineering Quarterly1451-93722217-74342017-01-01231677210.2298/CICEQ150521007G1451-93721600007GPreparation of titanium carbide powder from ilmenite concentrateGou Hai-Peng0Zhang Guo-Hua1Kuo-Chih Chou2University of Science and Technology Beijing, State Key Laboratory of Advanced Metallurgy, Beijing, China + University of Science and Technology Beijing, Collaborative Innovation Center of Universal Iron and Steel Technology, Beijing, ChinaUniversity of Science and Technology Beijing, State Key Laboratory of Advanced Metallurgy, Beijing, ChinaUniversity of Science and Technology Beijing, State Key Laboratory of Advanced Metallurgy, Beijing, China + University of Science and Technology Beijing, Collaborative Innovation Center of Universal Iron and Steel Technology, Beijing, ChinaA new process of producing titanium carbide powder from ilmenite concentrate was put forward. The ilmenite concentrate was reduced by graphite powder at 1500ºC for 6 hours, with the reduction products of TiC, Fe and MgO. The porous reduction products were agitation leached in ferric chloride solution at 25ºC for 60 minutes. After the filtration, TiC powder accompanied by little MgAl2O4 and Mg2SiO4 were obtained. Finally, the element Fe was recycled from the filtrate in the form of β-FeOOH after blowing air for 3 hours at 80ºC. The size of rod-like β-FeOOH particle was less than 1µm.http://www.doiserbia.nb.rs/img/doi/1451-9372/2017/1451-93721600007G.pdftianium carbideferric chloride solutionilmenite concentrateβ-FeOOH |
| spellingShingle | Gou Hai-Peng Zhang Guo-Hua Kuo-Chih Chou Preparation of titanium carbide powder from ilmenite concentrate Chemical Industry and Chemical Engineering Quarterly tianium carbide ferric chloride solution ilmenite concentrate β-FeOOH |
| title | Preparation of titanium carbide powder from ilmenite concentrate |
| title_full | Preparation of titanium carbide powder from ilmenite concentrate |
| title_fullStr | Preparation of titanium carbide powder from ilmenite concentrate |
| title_full_unstemmed | Preparation of titanium carbide powder from ilmenite concentrate |
| title_short | Preparation of titanium carbide powder from ilmenite concentrate |
| title_sort | preparation of titanium carbide powder from ilmenite concentrate |
| topic | tianium carbide ferric chloride solution ilmenite concentrate β-FeOOH |
| url | http://www.doiserbia.nb.rs/img/doi/1451-9372/2017/1451-93721600007G.pdf |
| work_keys_str_mv | AT gouhaipeng preparationoftitaniumcarbidepowderfromilmeniteconcentrate AT zhangguohua preparationoftitaniumcarbidepowderfromilmeniteconcentrate AT kuochihchou preparationoftitaniumcarbidepowderfromilmeniteconcentrate |