| Summary: | This work aims to clarify the effect of magnetic graphene oxide (GO) reorientation in a polymer matrix on the ionic conduction and methanol barrier properties of nanocomposite membrane electrolytes. Magnetic iron oxide (Fe3O4) nanoparticles were prepared and dispersed on GO nanosheets (GO-Fe3O4). The magnetic GO-Fe3O4 was imbedded into a quaternized polyvinyl alcohol (QPVA) matrix and crosslinked (CL-) with glutaraldehyde (GA) to obtain a polymeric nanocomposite. A magnetic field was applied in the through-plane direction during the drying and film formation steps. The CL-QPVA/GO-Fe3O4 nanocomposite membranes were doped with an alkali to obtain hydroxide-conducting electrolytes for direct methanol alkaline fuel cell (DMAFC) applications. The magnetic field-reoriented CL-QPVA/GO-Fe3O4 electrolyte demonstrated higher conductivity and lower methanol permeability than the unoriented CL-QPVA/GO-Fe3O4 membrane or the CL-QPVA film. The reoriented CL-QPVA/GO-Fe3O4 nanocomposite was used as the electrolyte in a DMAFC and resulted in a maximum power density of 55.4 mW·cm−2 at 60 °C, which is 73.7% higher than that of the composite without the magnetic field treatment (31.9 mW·cm−2). In contrast, the DMAFC using the CL-QPVA electrolyte generated only 22.4 mW·cm−2. This research proved the surprising benefits of magnetic-field-assisted orientation of GO-Fe3O4 in facilitating the ion conduction of a polymeric electrolyte.
|
|---|