| Summary: | Basic properties of sedge fibers from the seven-islands-sedge plant (<i>Cyperus malaccensis</i>) were investigated with possible application in reinforcing composite materials. A dimensional distribution and the effect of fiber diameter on density were investigated using gas pycnometry. The Weibull method, used to statistically analyze the acquired data from the diameter intervals, indicated an inverse dependence, where the thinnest fibers had the highest density values. The morphology of the fibers was obtained through scanning electron microscopy (SEM), in which a lower presence of defects was revealed in the thinner fibers, corroborating the inverse density dependence. In addition, the sedge fiber was characterized by differential scanning calorimetry and thermogravimetric analysis, which indicate an initial thermal degradation at around 241 °C. These results revealed for the first time that thinner sedge fibers might be promising reinforcement for polymer composites with a limit in temperature application.
|
|---|