Influence of Hardened Surface on Low Cycle Fatigue Characteristics at Tension-compression and Bending
This paper analyses electromechanical hardening of the steel parts surface, when in the contact area so called “white layer” is formed. The experiments were performed to show the influence of “white layer” on strength of the steel C45 specimens under low cycle loading. This paper analyses monotonic...
Main Authors: | , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Mendel University Press
2015-01-01
|
Series: | Acta Universitatis Agriculturae et Silviculturae Mendelianae Brunensis |
Subjects: | |
Online Access: | https://acta.mendelu.cz/63/5/1549/ |
_version_ | 1811256475309309952 |
---|---|
author | Artüras Sabaliauskas Sergėjus Rimovskis Petr Dostál |
author_facet | Artüras Sabaliauskas Sergėjus Rimovskis Petr Dostál |
author_sort | Artüras Sabaliauskas |
collection | DOAJ |
description | This paper analyses electromechanical hardening of the steel parts surface, when in the contact area so called “white layer” is formed. The experiments were performed to show the influence of “white layer” on strength of the steel C45 specimens under low cycle loading. This paper analyses monotonic and low cycle tension compression and pure bending characteristics of specimens with electromechanically hardened surface. The Performed experiments showed that under monotonic tension strength characteristics (σpr, σ02, σu) are increasing and strain characteristics (eu, ψ) are decreasing. During cyclic stress limited tension compression at low loading levels both the width of plastic strain hysteresis loop and accumulated plastic strain are decreasing, therefore the lifetime is increasing. Under pure bending this tendencies persist, but in this case the lifetime at all loading levels is larger than the lifetime at tension compression. |
first_indexed | 2024-04-12T17:40:47Z |
format | Article |
id | doaj.art-c9f07de10d964c7b9ca138af5da998a0 |
institution | Directory Open Access Journal |
issn | 1211-8516 2464-8310 |
language | English |
last_indexed | 2024-04-12T17:40:47Z |
publishDate | 2015-01-01 |
publisher | Mendel University Press |
record_format | Article |
series | Acta Universitatis Agriculturae et Silviculturae Mendelianae Brunensis |
spelling | doaj.art-c9f07de10d964c7b9ca138af5da998a02022-12-22T03:22:48ZengMendel University PressActa Universitatis Agriculturae et Silviculturae Mendelianae Brunensis1211-85162464-83102015-01-016351549155410.11118/actaun201563051549Influence of Hardened Surface on Low Cycle Fatigue Characteristics at Tension-compression and BendingArtüras Sabaliauskas0Sergėjus Rimovskis1Petr Dostál2Mechanical Engineering Department, Šiauliai University, Vilniaus g. 88, 76285 Šiauliai, LitvaMechanical Engineering Department, Šiauliai University, Vilniaus g. 88, 76285 Šiauliai, LitvaDepartment of Technology and Automobile Transport, Faculty of Agronomy, Mendel University in Brno, Zemědělská 1, 613 00 Brno, Czech RepublicThis paper analyses electromechanical hardening of the steel parts surface, when in the contact area so called “white layer” is formed. The experiments were performed to show the influence of “white layer” on strength of the steel C45 specimens under low cycle loading. This paper analyses monotonic and low cycle tension compression and pure bending characteristics of specimens with electromechanically hardened surface. The Performed experiments showed that under monotonic tension strength characteristics (σpr, σ02, σu) are increasing and strain characteristics (eu, ψ) are decreasing. During cyclic stress limited tension compression at low loading levels both the width of plastic strain hysteresis loop and accumulated plastic strain are decreasing, therefore the lifetime is increasing. Under pure bending this tendencies persist, but in this case the lifetime at all loading levels is larger than the lifetime at tension compression.https://acta.mendelu.cz/63/5/1549/low cycle fatiguepure bendingelectromechanical treatment |
spellingShingle | Artüras Sabaliauskas Sergėjus Rimovskis Petr Dostál Influence of Hardened Surface on Low Cycle Fatigue Characteristics at Tension-compression and Bending Acta Universitatis Agriculturae et Silviculturae Mendelianae Brunensis low cycle fatigue pure bending electromechanical treatment |
title | Influence of Hardened Surface on Low Cycle Fatigue Characteristics at Tension-compression and Bending |
title_full | Influence of Hardened Surface on Low Cycle Fatigue Characteristics at Tension-compression and Bending |
title_fullStr | Influence of Hardened Surface on Low Cycle Fatigue Characteristics at Tension-compression and Bending |
title_full_unstemmed | Influence of Hardened Surface on Low Cycle Fatigue Characteristics at Tension-compression and Bending |
title_short | Influence of Hardened Surface on Low Cycle Fatigue Characteristics at Tension-compression and Bending |
title_sort | influence of hardened surface on low cycle fatigue characteristics at tension compression and bending |
topic | low cycle fatigue pure bending electromechanical treatment |
url | https://acta.mendelu.cz/63/5/1549/ |
work_keys_str_mv | AT arturassabaliauskas influenceofhardenedsurfaceonlowcyclefatiguecharacteristicsattensioncompressionandbending AT sergejusrimovskis influenceofhardenedsurfaceonlowcyclefatiguecharacteristicsattensioncompressionandbending AT petrdostal influenceofhardenedsurfaceonlowcyclefatiguecharacteristicsattensioncompressionandbending |