Microwave Absorption Properties of Ceramics Based on BiFeO<sub>3</sub> Modified with Ho
Ceramic samples of Bi<sub>1−<i>x</i></sub>Ho<i><sub>x</sub></i>FeO<sub>3</sub>, where <i>x</i> = 0.00–0.50, with a modifier concentration variation step ∆<i>x</i> = 0.05–0.10, were prepared by a two-step solid-phase...
Main Authors: | Pavel Astafev, Konstantin Andryushin, Aleksey Pavelko, Alexander Lerer, Yakov Reizenkind, Ekaterina Glazunova, Lidiya Shilkina, Inna Andryushina, Alexandr Nagaenko, Larisa Reznichenko |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2024-01-01
|
Series: | Solids |
Subjects: | |
Online Access: | https://www.mdpi.com/2673-6497/5/1/5 |
Similar Items
-
Structural, Morphological and Dielectric Characterization of BiFeO<sub>3</sub> Fibers Grown by the LFZ Technique
by: Marina Vieira Peixoto, et al.
Published: (2023-06-01) -
Review on Resistive Switching Devices Based on Multiferroic BiFeO<sub>3</sub>
by: Xianyue Zhao, et al.
Published: (2023-04-01) -
XPS Study in BiFeO<sub>3</sub> Surface Modified by Argon Etching
by: Grecia Alejandra Gomez-Iriarte, et al.
Published: (2022-06-01) -
Exploring RF Magnetron Sputtering Growth Composite Thin Film BiFeO<sub>3</sub>-Bi<sub>2</sub>Fe<sub>4</sub>O<sub>9</sub> on C-Plane Al<sub>2</sub>O<sub>3</sub> Substrate
by: Suleiman Kallaev, et al.
Published: (2023-10-01) -
The Positive Temperature Coefficient of Resistivity in BiFeO<sub>3</sub> Films
by: Qianqian Yang, et al.
Published: (2022-03-01)