| Summary: | Abstract To obtain the distribution law of residual stress of 42CrMo steel processed by ultrasonic rolling extrusion process (UREP), according to the characteristics of the material treated by ultrasonic rolling extrusion process, 42CrMo steel quasi-static experiment and dynamic experiment are carried out, the improved Johnson–Cook model was proposed. Based on the 42CrMo constitutive equation, the ultrasonic rolling extrusion process finite element method and experiment of 42CrMo steel were carried out. The results show that the simulation value and experimental value of the residual stress distribution after ultrasonic rolling extrusion process of 42CrMo steel have good consistency, with the increase of static pressure and amplitude, the residual stress increases, and with the increase of rotational speed and feed speed, the residual stress decreases, a more accurate residual stress distribution law of ultrasonic rolling extrusion of 42CrMo steel is obtained.
|
|---|