| Summary: | Tape brazing constitutes a cost-effective alternative surface protection technology for complex-shaped surfaces. The study explores the characteristics of high-temperature brazed coatings using a cobalt-based powder deposited on a stainless-steel substrate in order to protect parts subjected to hot temperatures in a wear-exposed environment. Microstructural imaging corroborated with x-ray diffraction analysis showed a complex phased structure consisting of intermetallic Cr-Ni, C-Co-W Laves type, and chromium carbide phases. The surface properties of the coatings, targeting hot corrosion behavior, erosion, wear resistance, and microhardness, were evaluated. The high-temperature corrosion test was performed for 100 h at 750 °C in a salt mixture consisting of 25 wt.% NaCl + 75 wt.% Na<sub>2</sub>SO<sub>4</sub>. The degree of corrosion attack was closely connected with the exposure temperature, and the degradation of the material corresponding to the mechanisms of low-temperature hot corrosion. The erosion tests were carried out using alumina particles at a 90° impingement angle. The results, correlated with the microhardness measurements, have shown that Co-based coatings exhibited approximately 40% lower material loss compared to that of the steel substrate.
|
|---|