Hydrogen-Induced Phase Transformation and Microstructure Evolution for Ti-6Al-4V Parts Produced by Electron Beam Melting
In this paper, phase transitions and microstructure evolution in titanium Ti-6Al-4V alloy parts produced by electron beam melting (EBM) under hydrogenation was investigated. Hydrogenation was carried out at the temperature of 650 °C to the absolute hydrogen concentrations in the samples of 0...
Main Authors: | Natalia Pushilina, Alexey Panin, Maxim Syrtanov, Egor Kashkarov, Viktor Kudiiarov, Olga Perevalova, Roman Laptev, Andrey Lider, Andrey Koptyug |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2018-04-01
|
Series: | Metals |
Subjects: | |
Online Access: | http://www.mdpi.com/2075-4701/8/5/301 |
Similar Items
-
Laboratory X-ray Diffraction Complex for In Situ Investigations of Structural Phase Evolution of Materials under Gaseous Atmosphere
by: Maxim Syrtanov, et al.
Published: (2020-03-01) -
Surface Modification of the EBM Ti-6Al-4V Alloy by Pulsed Ion Beam
by: Natalia Pushilina, et al.
Published: (2021-03-01) -
Hydrogen Accumulation and Distribution in Titanium Coatings at Gas-Phase Hydrogenation
by: Andrey Lider, et al.
Published: (2020-07-01) -
New Ti–35Nb–7Zr–5Ta Alloy Manufacturing by Electron Beam Melting for Medical Application Followed by High Current Pulsed Electron Beam Treatment
by: Maria Surmeneva, et al.
Published: (2021-07-01) -
Spatial and Direction-Based Characterization of Microstructures and Microhardness of TA15 Titanium Alloy Produced by Electron Beam Melting
by: Jiangtao Ran, et al.
Published: (2021-04-01)