| Summary: | Mechanical activation of the calcium-rich fly ash formed in circulating fluidized bed combustion (CFBC) boilers was investigated to enhance the compressive strength performance of the pastes. We studied the effect of the activation on the physical, chemical, and mineral characteristics of fly ash and its pastes. Our study shows that already a short mechanical activation yields a 10-fold improvement in the compressive strength of the pastes, reaching 60 MPa after 90 days of curing without any chemical activation or blending. Mechanical activation caused fragmentation of large porous aggregates in the raw ash enhancing the physical properties and reactivity of fly ash particles. Similarly to calcium sulfoaluminate cements, the mechanical strength was provided by the formation of abundant ettringite and possibly C-(A)-S-H gel-like phase that created a highly compact microstructure. Our findings suggest that mechanically activated Ca-rich CFBC fly ash can be successfully used as an alternative binder.
|
|---|