Kinetics of Martensite Decomposition and Microstructure Stability of Ti-6246 during Rapid Heating to Service Temperatures
The aerospace alloy Ti-6246 was subjected to inductive heat treatments with high heating and quenching rates (up to 1500 K/s) while being applied to an in situ diffraction study at the HEMS beamline P07B at DESY. Thereby, the characterization of the emerging phases was possible at any point in the p...
Main Authors: | Anna-Lena Otte, Phuong Thao Mai, Andreas Stark, Markus Hoelzel, Michael Hofmann, Jens Gibmeier |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2023-02-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/13/3/484 |
Similar Items
-
Influence of Austenitisation Time and Temperature on Grain Size and Martensite Start of 51CrV4 Spring Steel
by: Anže Bajželj, et al.
Published: (2022-10-01) -
Investigating the role of the austenitizing temperature and cooling rate on the martensitic transformation kinetics in a SAE 9254 spring steel
by: Silvano Leal dos Santos, et al.
Published: (2024-03-01) -
Analyzing the Sintering Kinetics of Ti12.5Ta12.5Nb Alloy Produced by Powder Metallurgy
by: Rogelio Macias, et al.
Published: (2023-05-01) -
Comparative Study of the Tempering Behavior of Different Martensitic Steels by Means of In-Situ Diffractometry and Dilatometry
by: Martin Hunkel, et al.
Published: (2020-11-01) -
Study on Transformation Mechanism and Kinetics of α’ Martensite in TC4 Alloy Isothermal Aging Process
by: Hui Yu, et al.
Published: (2020-03-01)