Producing and Processing of Thin Al/Mg/Al Compounds
Research activities considering lightweight design are dedicated to substituting classic mild steels by light metal alloys. Magnesium is especially promising due to its beneficial strength–density ratio, but its industrial use is still limited due to, e.g., unfavorable corrosion properties. Thus, a...
Main Authors: | Maik Linnemann, Verena Psyk, Nico Kaden, Florens Kersten, Matthias Schmidtchen, Verena Kräusel, Martin Dix, Ulrich Prahl |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-11-01
|
Series: | Engineering Proceedings |
Subjects: | |
Online Access: | https://www.mdpi.com/2673-4591/26/1/8 |
Similar Items
-
Dissimilar micro friction stir welding of ultra-thin Mg AZ31 to Al 6061 sheets
by: Eisha Khalid, et al.
Published: (2022-11-01) -
Comparative Analysis of Electrohydraulic and Electromagnetic Sheet Metal Forming against the Background of the Application as an Incremental Processing Technology
by: Thomas Heggemann, et al.
Published: (2022-04-01) -
Sealing Technologies for the Manufacturing of Bipolar Plates via Active and Passive Hydroforming
by: André Albert, et al.
Published: (2022-11-01) -
Hydroforming of High-Strength Aluminum Tubes with Thermo-Mechanical Manufacturing Processes
by: Ricardo Trân, et al.
Published: (2022-11-01) -
Microstructure of the Bonding Zone Between AZ91 and AlSi17 Formed by Compound Casting
by: Mola R., et al.
Published: (2017-03-01)