Design of Ti<sub>2</sub>AlC/YSZ TBCs for more efficient in resisting CMAS attack
<p>Ti<sub>2</sub>AlC has been demonstrated as the promising protective layer material for thermal barrier coatings (TBCs) against calcium–magnesium–alumina–silicate (CMAS) attack. In this study, the reliability of Ti<sub>2</sub>AlC coatings against the CMAS corrosion wa...
Main Authors: | Lei Guo, Yanyan Li, Guang Li |
---|---|
Format: | Article |
Language: | English |
Published: |
Tsinghua University Press
2023-09-01
|
Series: | Journal of Advanced Ceramics |
Subjects: | |
Online Access: | https://www.sciopen.com/article/10.26599/JAC.2023.9220781 |
Similar Items
-
A New Al2O3‐Protected EB‐PVD TBC with Superior CMAS Resistance
by: Shiying Qin, et al.
Published: (2024-02-01) -
In-situ observation and mechanism of calcium–magnesium–alumina–silicate (CMAS) melts-induced degradation of RE2SiO5 (RE = Tb, Dy, Ho, Y, Er, Tm, and Yb) ceramics at 1500 °C
by: Zhilin Tian, et al.
Published: (2023-12-01) -
Crystallographic and TEM Features of a TBC/Ti<sub>2</sub>AlC MAX Phase Interface after 1300 °C Burner Rig Oxidation
by: James L. Smialek, et al.
Published: (2023-04-01) -
Mechanical Properties of Ti<sub>3</sub>AlC<sub>2</sub>/Cu Composites Reinforced by MAX Phase Chemical Copper Plating
by: Cong Chen, et al.
Published: (2024-02-01) -
Determination of residual stresses in thermal barrier coating due to the amount of CMAS infiltration
by: Pedro Yáñez Contreras, et al.
Published: (2020-11-01)