The Relationship of Fracture Mechanism between High Temperature Tensile Mechanical Properties and Particle Erosion Resistance of Selective Laser Melting Ti-6Al-4V Alloy
In this study, selective laser melting (SLM) Ti-6Al-4V is subjected to heat treatment for 4 h at 400 °C, 600 °C, and 800 °C, followed by air cooling. After heat treatment at 400 °C and 600 °C, the ductility was lower (strength increased). This was could b...
Main Authors: | Jun-Ren Zhao, Fei-Yi Hung, Truan-Sheng Lui, Yu-Lin Wu |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2019-04-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/9/5/501 |
Similar Items
-
Erosion Resistance and Particle Erosion-Induced Tensile Embrittlement of 3D-Selective Laser Melting Inconel 718 Superalloy
by: Jun-Ren Zhao, et al.
Published: (2019-12-01) -
Slurry Erosion–Corrosion Characteristics of As-Built Ti-6Al-4V Manufactured by Selective Laser Melting
by: Saleh Ahmed Aldahash, et al.
Published: (2020-09-01) -
Improving the applicability of wear-resistant Al–10Si–0.5 Mg alloy obtained through selective laser melting with T6 treatment in high-temperature, and high-wear environments
by: Kuan-Jen Chen, et al.
Published: (2020-07-01) -
Al<sub>2</sub>O<sub>3</sub> Particle Erosion Induced Phase Transformation: Structure, Mechanical Property, and Impact Toughness of an SLM Al-10Si-Mg Alloy
by: Bo-Chin Huang, et al.
Published: (2021-08-01) -
Particle Erosion Induced Phase Transformation of Different Matrix Microstructures of Powder Bed Fusion Ti-6Al-4V Alloy Flakes
by: Jun-Ren Zhao, et al.
Published: (2019-06-01)