Caracterización de espumas de pizarra con adiciones de clínquer de cemento
The decomposition of constituents of slates under non-oxidizing atmosphere leads to the manufacturing of foams. Thus die pressing at 80MPa of slates powders (particle size <80 microns) mixed with a solid agglomerate, allows a green density close to 1,8 g/cm3 . The heating of compacts under N2...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2007-04-01
|
| Series: | Boletín de la Sociedad Española de Cerámica y Vidrio |
| Subjects: | |
| Online Access: | http://ceramicayvidrio.revistas.csic.es/index.php/ceramicayvidrio/article/view/254/271 |
| _version_ | 1819209873181638656 |
|---|---|
| author | Cambronero, L. E.G. Ruiz-Román, J. M. Ruiz-Prieto, J. M. |
| author_facet | Cambronero, L. E.G. Ruiz-Román, J. M. Ruiz-Prieto, J. M. |
| author_sort | Cambronero, L. E.G. |
| collection | DOAJ |
| description | The decomposition of constituents of slates under non-oxidizing atmosphere leads to the manufacturing of foams. Thus die pressing at 80MPa of slates powders (particle size <80 microns) mixed with a solid agglomerate, allows a green density close to 1,8 g/cm3 . The heating of compacts under N2-5%H2 atmosphere allows to reach a final density of 2,2 g/cm3 at 1050ºC, meanwhile at 1150ºC the compact foaming leads to densities lower than 0,4 g/cm3. Clínquer addition (5% and 10%) modifies the foam density and pore size at 1150ºC. It is necessary to increase the sintering temperature up to 1175ºC to achieve densities close to 0,4 g/cm3 when a 10% of Clínquer is added. The foams with Clínquer shows a high pore size and a compression strength within the range of glass foams: 0.4-1.5MPa.<br><br>La descomposición de los componentes de la Pizarra durante su calentamiento en condiciones no oxidantes conduce a la obtención de espumas. Así, mediante la compactación en matriz a 80MPa de polvos de Pizarra de menos de 80 μm de tamaño de partícula y con adición de un aglomerante, se obtiene una densidad en verde próxima a 1,8 g/cm3. El calentamiento de estos compactos en atmósfera de N2-5% H2 permite alcanzar densidades de 2,2 g/cm3 a 1100ºC , mientras que a 1150ºC la espumación del compacto conduce a densidades inferiores a 0,4 g/cm3. La adición de Clínquer de cemento Portland (5% y 10% en peso) modifica la densidad de la espuma a 1150ºC , teniendo que elevarse la temperatura de sinterización a 1175 ºC para alcanzarse espumas con densidades próximas a 0,4 g/cm3 con un 10% de Clínquer. Estas espumas con Clínquer presentan un elevado tamaño de poro, así como una resistencia a compresión en el intervalo de resistencias de los vidrios espumados: 0,4-1,5MPa. |
| first_indexed | 2024-12-23T06:02:12Z |
| format | Article |
| id | doaj.art-d48cc756ddb74539a2fbb28da42dc066 |
| institution | Directory Open Access Journal |
| issn | 0366-3175 |
| language | English |
| last_indexed | 2024-12-23T06:02:12Z |
| publishDate | 2007-04-01 |
| publisher | Elsevier |
| record_format | Article |
| series | Boletín de la Sociedad Española de Cerámica y Vidrio |
| spelling | doaj.art-d48cc756ddb74539a2fbb28da42dc0662022-12-21T17:57:40ZengElsevierBoletín de la Sociedad Española de Cerámica y Vidrio0366-31752007-04-014628690Caracterización de espumas de pizarra con adiciones de clínquer de cementoCambronero, L. E.G.Ruiz-Román, J. M.Ruiz-Prieto, J. M.The decomposition of constituents of slates under non-oxidizing atmosphere leads to the manufacturing of foams. Thus die pressing at 80MPa of slates powders (particle size <80 microns) mixed with a solid agglomerate, allows a green density close to 1,8 g/cm3 . The heating of compacts under N2-5%H2 atmosphere allows to reach a final density of 2,2 g/cm3 at 1050ºC, meanwhile at 1150ºC the compact foaming leads to densities lower than 0,4 g/cm3. Clínquer addition (5% and 10%) modifies the foam density and pore size at 1150ºC. It is necessary to increase the sintering temperature up to 1175ºC to achieve densities close to 0,4 g/cm3 when a 10% of Clínquer is added. The foams with Clínquer shows a high pore size and a compression strength within the range of glass foams: 0.4-1.5MPa.<br><br>La descomposición de los componentes de la Pizarra durante su calentamiento en condiciones no oxidantes conduce a la obtención de espumas. Así, mediante la compactación en matriz a 80MPa de polvos de Pizarra de menos de 80 μm de tamaño de partícula y con adición de un aglomerante, se obtiene una densidad en verde próxima a 1,8 g/cm3. El calentamiento de estos compactos en atmósfera de N2-5% H2 permite alcanzar densidades de 2,2 g/cm3 a 1100ºC , mientras que a 1150ºC la espumación del compacto conduce a densidades inferiores a 0,4 g/cm3. La adición de Clínquer de cemento Portland (5% y 10% en peso) modifica la densidad de la espuma a 1150ºC , teniendo que elevarse la temperatura de sinterización a 1175 ºC para alcanzarse espumas con densidades próximas a 0,4 g/cm3 con un 10% de Clínquer. Estas espumas con Clínquer presentan un elevado tamaño de poro, así como una resistencia a compresión en el intervalo de resistencias de los vidrios espumados: 0,4-1,5MPa.http://ceramicayvidrio.revistas.csic.es/index.php/ceramicayvidrio/article/view/254/271SlatesClínquerglass foamPizarrasClínquervidrio espumado |
| spellingShingle | Cambronero, L. E.G. Ruiz-Román, J. M. Ruiz-Prieto, J. M. Caracterización de espumas de pizarra con adiciones de clínquer de cemento Boletín de la Sociedad Española de Cerámica y Vidrio Slates Clínquer glass foam Pizarras Clínquer vidrio espumado |
| title | Caracterización de espumas de pizarra con adiciones de clínquer de cemento |
| title_full | Caracterización de espumas de pizarra con adiciones de clínquer de cemento |
| title_fullStr | Caracterización de espumas de pizarra con adiciones de clínquer de cemento |
| title_full_unstemmed | Caracterización de espumas de pizarra con adiciones de clínquer de cemento |
| title_short | Caracterización de espumas de pizarra con adiciones de clínquer de cemento |
| title_sort | caracterizacion de espumas de pizarra con adiciones de clinquer de cemento |
| topic | Slates Clínquer glass foam Pizarras Clínquer vidrio espumado |
| url | http://ceramicayvidrio.revistas.csic.es/index.php/ceramicayvidrio/article/view/254/271 |
| work_keys_str_mv | AT cambroneroleg caracterizaciondeespumasdepizarraconadicionesdeclinquerdecemento AT ruizromanjm caracterizaciondeespumasdepizarraconadicionesdeclinquerdecemento AT ruizprietojm caracterizaciondeespumasdepizarraconadicionesdeclinquerdecemento |