Microstructural Changes and Strengthening of Austenitic Stainless Steels during Rolling at 473 K
The microstructural changes in 304L and 316L austenitic stainless steels during plate rolling with 95% rolling reduction at a temperature of 473 K and their effect on strengthening were studied. The microstructure evolution was associated with deformation twinning and microshear banding. The latter...