Removal of Sodium from Vanadium Tailings by Calcification Roasting in Reducing Atmosphere
Vanadium tailings from vanadium extraction by a sodium roasting process are solid waste and cannot be used in sintering and ironmaking due to their high sodium content. In this paper, a calcification and reduction roasting process was proposed to remove sodium from vanadium tailings. The effects of...
Main Authors: | Chao Wang, Yufeng Guo, Shuai Wang, Feng Chen, Lingzhi Yang, Yu Zheng |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2023-01-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/16/3/986 |
Similar Items
-
Estimation of vanadium removal from calcification roasting-acid leaching tailings using ultrasonic-H2C2O4 synergistic technology
by: Haoyu Li, et al.
Published: (2023-12-01) -
Efficient Separation of Silicon and Vanadium by Sodium Roasting-Water Leaching from Vanadium Slag and CaV<sub>2</sub>O<sub>6</sub> Preparation
by: Changqing Li, et al.
Published: (2021-03-01) -
Preparation Process of High Strength Ceramsite from Acid Leaching Vanadium Tailing
by: Yonghai Wang, et al.
Published: (2022-06-01) -
Selective sulfuric acid cyclic leaching of vanadium from the calcification roasting pellets of vanadium titanomagnetite
by: Zhixiang Wang, et al.
Published: (2023-03-01) -
A Novel Technology for Recovery and Separation of Vanadium and Chromium from Vanadium-Chromium Reducing Residue
by: Hao Peng, et al.
Published: (2019-12-01)