| Summary: | This study analyzed the dentin shear bond strength (SBS) of an etch-and-rinse (ER) or a self-etch (SE) adhesive incorporated with multifunctional polyhedral oligomeric silsesquioxanes (MA-POSS-8). An ER adhesive (Solobond Plus, VOCO GmbH, Cuxhaven, Germany) and a universal adhesive applied in SE mode (Scotchbond Universal, 3M, St. Paul, MN, USA) were infiltrated with MA-POSS-8 (Hybrid Plastics Inc., Hattiesburg, MS, USA) at 5 wt.% or 10 wt.%. Pure adhesives served as controls. Bovine dentin specimens were conditioned with one of the adhesives prior to the application of a nano-hybrid composite (Venus Diamond A3, Kulzer, Hanau, Germany). SBS and failure modes were determined after water storage for 24 h, 6 months, 12 months, or 24 months (each subgroup n = 20). Statistical analysis was performed using ANOVAs, Weibull statistics, and χ<sup>2</sup> tests (<i>p</i> < 0.05). SBSs for the control groups after 24 h were 17.4 ± 4.9 MPa for the ER adhesive and 19.1 ± 5.2 MPa for the universal adhesive. After 24 months, the SBS of the ER adhesive was significantly higher for 5 wt.% MA-POSS-8 (17.9 ± 5.1 MPa) than for the control group (14.6 ± 3.6 MPa) and 10 wt.% MA-POSS-8 (12.8 ± 4.1 MPa), and more cohesive failures were observed. The SBS of the universal adhesive increased during aging, irrespective of the MA-POSS-8 concentration. 5 wt.% MA-POSS-8 improves the SBS of the ER adhesive and does not impair the SBS of the SE adhesive.
|
|---|