Influence of Boron on Crystallization and Microstructure of Ductile Cast Iron
The objective of the research was to determine the influence of boron on the crystallization process and microstructure of ductile cast iron. In the case of ductile cast iron it is a vital issue because even as little as trace presence of boron changes the properties of ductile cast iron in a signif...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Polish Academy of Sciences
2017-06-01
|
| Series: | Archives of Foundry Engineering |
| Subjects: | |
| Online Access: | http://www.degruyter.com/view/j/afe.2017.17.issue-2/afe-2017-0043/afe-2017-0043.xml?format=INT |
| _version_ | 1797707620179509248 |
|---|---|
| author | Dojka R. Studnicki A. |
| author_facet | Dojka R. Studnicki A. |
| author_sort | Dojka R. |
| collection | DOAJ |
| description | The objective of the research was to determine the influence of boron on the crystallization process and microstructure of ductile cast iron. In the case of ductile cast iron it is a vital issue because even as little as trace presence of boron changes the properties of ductile cast iron in a significant way. With the use of a new ATD-4 (TDA) tester and CRYSTALDIGRPAH converter it was possible to measure the crystallization process parameters of the same alloy with four different contents of boron in one mould. Four samples with different boron contents were extracted, their microhardness was measured and quantitative analysis of microstructure was conducted. Obtained results allowed to state that with increasing content of boron the amount of graphite precipitates decreases, the amount of pearlite precipitates increases, the shape of graphite precipitates deteriorates and hardness increases. It is also planned to perform additional testings with boron contents between previously tested values. |
| first_indexed | 2024-03-12T06:09:04Z |
| format | Article |
| id | doaj.art-dba7ff19453d4a19bfac9a25dffd2d2e |
| institution | Directory Open Access Journal |
| issn | 2299-2944 |
| language | English |
| last_indexed | 2024-03-12T06:09:04Z |
| publishDate | 2017-06-01 |
| publisher | Polish Academy of Sciences |
| record_format | Article |
| series | Archives of Foundry Engineering |
| spelling | doaj.art-dba7ff19453d4a19bfac9a25dffd2d2e2023-09-03T03:20:28ZengPolish Academy of SciencesArchives of Foundry Engineering2299-29442017-06-01172152010.1515/afe-2017-0043afe-2017-0043Influence of Boron on Crystallization and Microstructure of Ductile Cast IronDojka R.0Studnicki A.1Department of Foundry, Silesian University of Technology , Towarowa 7, 44-100 Gliwice, PolandDepartment of Foundry, Silesian University of Technology , Towarowa 7, 44-100 Gliwice, PolandThe objective of the research was to determine the influence of boron on the crystallization process and microstructure of ductile cast iron. In the case of ductile cast iron it is a vital issue because even as little as trace presence of boron changes the properties of ductile cast iron in a significant way. With the use of a new ATD-4 (TDA) tester and CRYSTALDIGRPAH converter it was possible to measure the crystallization process parameters of the same alloy with four different contents of boron in one mould. Four samples with different boron contents were extracted, their microhardness was measured and quantitative analysis of microstructure was conducted. Obtained results allowed to state that with increasing content of boron the amount of graphite precipitates decreases, the amount of pearlite precipitates increases, the shape of graphite precipitates deteriorates and hardness increases. It is also planned to perform additional testings with boron contents between previously tested values.http://www.degruyter.com/view/j/afe.2017.17.issue-2/afe-2017-0043/afe-2017-0043.xml?format=INTSolidification processMetallographyDuctile cast ironBoronTDA |
| spellingShingle | Dojka R. Studnicki A. Influence of Boron on Crystallization and Microstructure of Ductile Cast Iron Archives of Foundry Engineering Solidification process Metallography Ductile cast iron Boron TDA |
| title | Influence of Boron on Crystallization and Microstructure of Ductile Cast Iron |
| title_full | Influence of Boron on Crystallization and Microstructure of Ductile Cast Iron |
| title_fullStr | Influence of Boron on Crystallization and Microstructure of Ductile Cast Iron |
| title_full_unstemmed | Influence of Boron on Crystallization and Microstructure of Ductile Cast Iron |
| title_short | Influence of Boron on Crystallization and Microstructure of Ductile Cast Iron |
| title_sort | influence of boron on crystallization and microstructure of ductile cast iron |
| topic | Solidification process Metallography Ductile cast iron Boron TDA |
| url | http://www.degruyter.com/view/j/afe.2017.17.issue-2/afe-2017-0043/afe-2017-0043.xml?format=INT |
| work_keys_str_mv | AT dojkar influenceofborononcrystallizationandmicrostructureofductilecastiron AT studnickia influenceofborononcrystallizationandmicrostructureofductilecastiron |