Interaction Influence of Flaw and Stress on L<sub>cr</sub> Wave Acoustoelastic Coefficient of Carbon Steel
Based on L<sub>cr</sub> wave acoustoelastic theory, the influence mechanism of blind-hole on stress evaluation with L<sub>cr</sub> wave was discussed. Combined with equivalent method, the blind-holes with different diameters were preset, the difference in time of flight betwe...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Journal of Materials Engineering
2017-07-01
|
| Series: | Cailiao gongcheng |
| Subjects: | |
| Online Access: | http://jme.biam.ac.cn/CN/Y2017/V45/I7/97 |
| Summary: | Based on L<sub>cr</sub> wave acoustoelastic theory, the influence mechanism of blind-hole on stress evaluation with L<sub>cr</sub> wave was discussed. Combined with equivalent method, the blind-holes with different diameters were preset, the difference in time of flight between L<sub>cr</sub> wave was calculated by cross correlation coefficient function, the L<sub>cr</sub> wave acoustoelastic coefficient was determined with linear fitting function, the influence mechanism of blind-hole diameter on L<sub>cr</sub> wave acoustoelastic coefficient was clarified based on the elastic plastic deformation theory and stress concentration theory of hole. The results show that when the diameter of blind-hole is different, the change rule of the difference in time of flight between L<sub>cr</sub> wave is basically the same as stress increases, the difference in time of flight between L<sub>cr</sub> wave increases linearly as stress increases, while the nonlinear feature is also gradually obvious, the maximum stress in linear stage is less than the yield strength of specimen, the L<sub>cr</sub> wave acoustoelastic coefficient decreases gradually as blind-hole diameter increases, and it tends to be constant. The analysis shows that the stress concentration is seen as the main reason for above results, anisotropic structure of specimen and blind-hole depth are also the important reasons for that. |
|---|---|
| ISSN: | 1001-4381 1001-4381 |