Microstructural Evolution and Element Partitioning in the Phase Transformation of Ti-17 Alloy under Continuous Heating and Cooling Conditions
The microstructural evolution and alloying element partitioning in the α + β ↔ β phase transformation of Ti-17 alloy were explored under continuous heating and cooling conditions using the dilatometric method. Scanning electron microscopy and transmission electron microscopy were used to evaluate mi...
Main Authors: | Xudong An, Xin Cai, Mingpan Wan, Min Lei, Chaowen Huang, Fei Zhao, Fang Huang |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-08-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/10/8/1054 |
Similar Items
-
Rapid Cooling and Solidification Microstructure of Argon Atomized Ti-48Al Alloy Droplets
by: BAO Ying, et al.
Published: (2018-12-01) -
Precipitation Behavior of O Phase during Continuous Cooling of Ti-22Al-25Nb Alloy
by: Dong Li, et al.
Published: (2022-02-01) -
Evolution of microstructure, mechanical properties and corrosion behaviors using cooling rate regulation in a novel ZrTi-based alloy
by: Huicong Dong, et al.
Published: (2020-05-01) -
Study on the deformation mechanism of Ti–10Mo–1Fe solid-solution alloys with different cooling rates
by: Beite Gao, et al.
Published: (2023-03-01) -
Study on the Changing Law of Cutting and Ultrasonic Strengthening Surface Integrity during Fatigue of Ti-17 Alloy
by: Zheng Zhou, et al.
Published: (2022-11-01)