A new production technique for wear resistant ring-hammers
Based on a great number of laboratory experiments, a new technique has been developed for producing wear resistant ring-hammers. In this technology, lost foam casting with iron sand was combined to make mold; a special alloy was used to inoculate the molten steel, and proper heat treatment was used...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Foundry Journal Agency
2011-11-01
|
| Series: | China Foundry |
| Subjects: | |
| Online Access: | http://www.foundryworld.com/uploadfile/2011122147345933.pdf |
| _version_ | 1818144814333427712 |
|---|---|
| author | Li Shifeng Zhang Dinghua Bu Kun |
| author_facet | Li Shifeng Zhang Dinghua Bu Kun |
| author_sort | Li Shifeng |
| collection | DOAJ |
| description | Based on a great number of laboratory experiments, a new technique has been developed for producing wear resistant ring-hammers. In this technology, lost foam casting with iron sand was combined to make mold; a special alloy was used to inoculate the molten steel, and proper heat treatment was used to further improve mechanical properties of wear resistant ring-hammers. The influence of this new production technology on the microstructure and mechanical properties of wear resistant ring-hammers was studied. Results show that iron sand molding, having the inherent characteristic of sand molding, changes the type of metallic compounds, refines crystal grains and increases the fineness of microstructure. Practical experience verified that the properties of the ring-hammers produced with this new technique are as follows: tensile strength (Rm) 720 MPa, impact toughness (ak) > 210 J•cm-2 and hardness > 200 HB. After water quenching from 1,080℃ (holding for 4 h) and tempering at 320℃ for 3 h, the best wear resistance is obtained, and the wear resistance is 1.6 times higher than that of common high manganese ring-hammers. |
| first_indexed | 2024-12-11T11:53:32Z |
| format | Article |
| id | doaj.art-e0786d6b40ab441296e74f596c42d7ac |
| institution | Directory Open Access Journal |
| issn | 1672-6421 |
| language | English |
| last_indexed | 2024-12-11T11:53:32Z |
| publishDate | 2011-11-01 |
| publisher | Foundry Journal Agency |
| record_format | Article |
| series | China Foundry |
| spelling | doaj.art-e0786d6b40ab441296e74f596c42d7ac2022-12-22T01:08:17ZengFoundry Journal AgencyChina Foundry1672-64212011-11-0184407412A new production technique for wear resistant ring-hammersLi ShifengZhang DinghuaBu KunBased on a great number of laboratory experiments, a new technique has been developed for producing wear resistant ring-hammers. In this technology, lost foam casting with iron sand was combined to make mold; a special alloy was used to inoculate the molten steel, and proper heat treatment was used to further improve mechanical properties of wear resistant ring-hammers. The influence of this new production technology on the microstructure and mechanical properties of wear resistant ring-hammers was studied. Results show that iron sand molding, having the inherent characteristic of sand molding, changes the type of metallic compounds, refines crystal grains and increases the fineness of microstructure. Practical experience verified that the properties of the ring-hammers produced with this new technique are as follows: tensile strength (Rm) 720 MPa, impact toughness (ak) > 210 J•cm-2 and hardness > 200 HB. After water quenching from 1,080℃ (holding for 4 h) and tempering at 320℃ for 3 h, the best wear resistance is obtained, and the wear resistance is 1.6 times higher than that of common high manganese ring-hammers.http://www.foundryworld.com/uploadfile/2011122147345933.pdfnew production technologywear resistant ring-hammercompound modificationlost foam casting with iron sand molding |
| spellingShingle | Li Shifeng Zhang Dinghua Bu Kun A new production technique for wear resistant ring-hammers China Foundry new production technology wear resistant ring-hammer compound modification lost foam casting with iron sand molding |
| title | A new production technique for wear resistant ring-hammers |
| title_full | A new production technique for wear resistant ring-hammers |
| title_fullStr | A new production technique for wear resistant ring-hammers |
| title_full_unstemmed | A new production technique for wear resistant ring-hammers |
| title_short | A new production technique for wear resistant ring-hammers |
| title_sort | new production technique for wear resistant ring hammers |
| topic | new production technology wear resistant ring-hammer compound modification lost foam casting with iron sand molding |
| url | http://www.foundryworld.com/uploadfile/2011122147345933.pdf |
| work_keys_str_mv | AT lishifeng anewproductiontechniqueforwearresistantringhammers AT zhangdinghua anewproductiontechniqueforwearresistantringhammers AT bukun anewproductiontechniqueforwearresistantringhammers AT lishifeng newproductiontechniqueforwearresistantringhammers AT zhangdinghua newproductiontechniqueforwearresistantringhammers AT bukun newproductiontechniqueforwearresistantringhammers |