Influence of White Etching Bands Formation on Integrity of Rolling Element Bearings

Influence of White Etching Bands Formation on Integrity of Rolling Element Bearings

The development of subsurface microstructural alterations known as dark etching regions (DERs) and white etching bands (WEBs) in rolling element bearings due to rolling contact fatigue have been investigated for the past eight decades, focusing on their initiation and formation mechanisms. They have...

书目详细资料
Main Authors:	Mostafa El Laithy, Ling Wang, Terry J. Harvey, Bernd Vierneusel
格式:	文件
语言:	English
出版:	Japanese Society of Tribologists 2023-10-01
丛编:	Tribology Online
主题:	rolling element bearing rolling contact fatigue white etching bands cracks inclusions steel
在线阅读:	https://www.jstage.jst.go.jp/article/trol/18/6/18_373/_pdf/-char/en

相似书籍

A Study on Early Stages of White Etching Crack Formation under Full Lubrication Conditions
由: Walter Holweger, et al.
出版: (2022-02-01)

Influence of Slip and Lubrication Regime on the Formation of White Etching Cracks on a Two-Disc Test Rig
由: Francisco Gutiérrez Guzmán, et al.
出版: (2018-01-01)

Evolution of White Etching Bands in 100Cr6 Bearing Steel under Rolling Contact-Fatigue
由: Hanwei Fu, et al.
出版: (2019-04-01)

Rolling Contact Fatigue-Related Microstructural Alterations in Bearing Steels: A Brief Review
由: Hongxiang Yin, et al.
出版: (2022-05-01)

Confirming Debonding of Non-Metallic Inclusions as an Important Factor in Damage Initiation in Bearing Steel
由: Ksenija Nikolic, et al.
出版: (2023-06-01)

Influence of white etching layer on rolling contact behavior at wheel-rail interface
由: Qinglin Lian, et al.
出版: (2020-05-01)

The Influence of Peripheral Components in Test Rig Creation of White Etching Cracks
由: Jürgen Wranik, et al.
出版: (2024-02-01)

Influence of Tribolayer on Rolling Bearing Fatigue Performed on an FE8 Test Rig—A Follow-up
由: Joerg W. H. Franke, et al.
出版: (2023-03-01)

A study of white etching crack formation by compression-torsion experiments
由: S. Averbeck, et al.
出版: (2016-10-01)

A study of white etching crack formation by compression-torsion experiments
由: S. Averbeck, et al.
出版: (2016-10-01)

Characterisation of white etching area in a ball of deep groove ball bearing obtained from the market
由: Susumu MIYAKAWA, et al.
出版: (2018-11-01)

Mechanism of Microstructural Alterations of M50 Bearing Steel during Rolling Contact Fatigue under High Loads
由: Jun Guo, et al.
出版: (2023-04-01)

Spalling Life Prediction for Rolling Bearings Using a Model with Stress Intensity Factor and Statistical Evaluation of Non-Metallic Inclusions
由: Hiroki Komata, et al.
出版: (2024-11-01)

Propagation of Large Spalls in Rolling Bearings
由: Guillermo E. Morales-Espejel, et al.
出版: (2019-12-01)

A Validated Computational Study of Lubricants under White Etching Crack Conditions Exposed to Electrical Fields
由: Walter Holweger, et al.
出版: (2023-01-01)

NUMERICAL AND ANALYTICAL PROBLEMS OF FATIGUE STRENGTH IN ROLLING BEARINGS
由: Paweł ROMANOWICZ, et al.
出版: (2014-06-01)

A Study on Decisive Early Stages in White Etching Crack Formation Induced by Lubrication
由: Jürgen Wranik, et al.
出版: (2022-05-01)

Prediction of Work Hardening in Bearing Steels Undergoing Rolling Contact Loading with a Dislocation-Based Model
由: Hongxiang Yin, et al.
出版: (2022-03-01)

RELATIONSHIP BETWEEN ROLLING AND SLIP RESISTANCE IN ROLLING BEARINGS
由: L. M. Bondarenko, et al.
出版: (2016-06-01)

The Effects of Hydrogen on Microstructural Change and Surface Originated Flaking in Rolling Contact Fatigue
由: Hideyuki Uyama, et al.
出版: (2011-01-01)

Rolling contact phenomena : proceedings
由: Symposium on Rolling Contact Phenomena, (4th : October 10-11, 1960 : General Motors Research Laboratories, Warren, Michigan), et al.
出版: (1962)

Effect of Mechanical Properties of Rail and Wheel on Wear and Rolling Contact Fatigue
由: Jung-Won Seo, et al.
出版: (2022-04-01)

Effect of small defect on the flaking strength of rolling bearings (Part 2: Evaluation of the flaking strength of rolling bearing having a small drilled hole based on stress intensity factor)
由: Sho HASHIMOTO, et al.
出版: (2017-07-01)

Numerical analysis of hydrogen-assisted rolling-contact fatigue of wind turbine bearings
由: J. Toribio, et al.
出版: (2014-09-01)

Effect of defect length on rolling contact fatigue crack propagation in high strength steel
由: T. Makino, et al.
出版: (2015-09-01)

In situ observation of rolling contact fatigue cracks by laminography using ultrabright synchrotron radiation
由: Y. Nakai, et al.
出版: (2015-09-01)

Formation mechanism and microstructure evolution of light etched region during rolling contact fatigue in M50 steel
由: Xingyu Lu, et al.
出版: (2023-05-01)

Research of Fault Diagnosis Method of Rolling Bearing based on CEEMDAN-DRT
由: Bie Fengfeng, et al.
出版: (2020-04-01)

Numerical analysis of hydrogen-assisted rolling-contact fatigue of wind turbine bearings
由: J. Toribio, et al.
出版: (2014-10-01)

Bearing technology : analysis, development and testing
由: International Off Highway & Powerplant Congress & Exposition MECCA (1985 : Milwaukee), et al.
出版: (1985)

Advanced dynamics of rolling elements/
由: 373645 Gupta, Pradeep K.
出版: (1984)

History of Rolling Bearings
由: Bo Jacobson
出版: (2011-01-01)

Rolling contact fatigue modelling and life prediction for aeroengine bearing steels
由: FU Hanwei, et al.
出版: (2024-10-01)

Formation Mechanisms and Crack Propagation Behaviors of White Etching Layers and Brown Etching Layers on Raceways of Failure Bearings
由: Xiaochen Zhang, et al.
出版: (2024-02-01)

Study of the Plastic Behavior of Rough Bearing Surfaces Using a Half-Space Contact Model and the Fatigue Life Estimation According to the Fatemi–Socie Model
由: Flavien Foko Foko, et al.
出版: (2023-03-01)

Studies on the Influence of Residual Stresses on the Fatigue Life of Rolling Bearings in Dependence on the Production Processes
由: Florian Pape, et al.
出版: (2020-07-01)

RESEARCH ON ROLLING BEARING WEAR PROBLEMS AND PROSPECT
由: ZHAO LiJuan, et al.
出版: (2016-01-01)

Role of multiaxial stress state in the hydrogen-assisted rolling-contact fatigue in bearings for wind turbines
由: J. Toribio, et al.
出版: (2015-06-01)

DYNAMIC CHARACTERISTICS OF INTERNAL CONTACT OF ROLLING BEARINGS UNDER DIFFERENT DEGREES OF FAILURE
由: TU WenBing, et al.
出版: (2020-01-01)

Role of multiaxial stress state in the hydrogen-assisted rolling-contact fatigue in bearings for wind turbines
由: J. Toribio, et al.
出版: (2015-07-01)