The footprint of surface modification treatments on the corrosion-fatigue of AA7075-T651
Different manufacturing and surface modification treatments distinctively affect the surface characteristics and microstructure of the workpiece, having a different impact on their effective life-span. The corrosion-fatigue behavior of as-machined (wire-EDM), blasted and anodized aluminum alloy 7075...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2018-01-01
|
| Series: | MATEC Web of Conferences |
| Online Access: | https://doi.org/10.1051/matecconf/201818803011 |
| Summary: | Different manufacturing and surface modification treatments distinctively affect the surface characteristics and microstructure of the workpiece, having a different impact on their effective life-span. The corrosion-fatigue behavior of as-machined (wire-EDM), blasted and anodized aluminum alloy 7075-T651 was investigated using 3.5wt% NaCl aqueous solution and distilled water as corrosive media. An in-situ corrosion-fatigue device capable of producing cyclic loads in a corrosive solution was employed, coupled with FEM analysis. Blasting process offered a prolongation of the corrosion-fatigue life-span in both corrosive media, when compared to the as-machined samples under identical conditions. Anodizing had a deleterious effect in all the examined cases. |
|---|---|
| ISSN: | 2261-236X |