Magnetic softening of the Fe83Si3B11P2Cu1 amorphous/nanocrystalline alloys with large-size pre-existing α-Fe grains by high heating-rate annealing
The microstructure and soft magnetic properties of Fe83Si3B11P2Cu1 (at.%) nanocrystalline ribbons with different thicknesses up to 40 μm obtained by annealing the amorphous/nanocrystalline precursors at various heating rates (HRs) were studied. It was found that the thicker melt-spun alloy ribbons c...