Preparation of Magnetically Driven Nickel Phosphide Nanowires and Their Electrochemical Properties
In this study, nickel phosphide nanowires with various structures and compositions were fabricated for the first time via magnetically-assisted liquid phase synthesis. The curvature and aspect ratio of the nanowires largely depended on the strength of the magnetic field applied during synthesis. The...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2021-12-01
|
| Series: | Applied Sciences |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2076-3417/12/1/49 |
| Summary: | In this study, nickel phosphide nanowires with various structures and compositions were fabricated for the first time via magnetically-assisted liquid phase synthesis. The curvature and aspect ratio of the nanowires largely depended on the strength of the magnetic field applied during synthesis. Their phosphorus content together with the morphology were significantly modified according to the pH and reducing agent concentration. Nanowires with different structures and phosphorus contents were preliminarily tested for their capabilities to serve in general electrochemical applications. The degree of reaction (i.e., amount of reaction charge) increased with increases in the reaction area and phosphorus content of the nanowires. The rate characteristics of the reaction showed a peculiar increasing trend for a small reaction surface area and low phosphorus content. A change in the ohmic overpotential according to the nanowire curvature (aspect ratio) and porosity was suggested to be the reason for this unusual trend. Electrodes with high phosphorus contents or high reaction surface areas rapidly deteriorated during repetitive redox reactions. Based on the results for the degradation degree, the effect of the reaction surface area dominated that of the phosphorus content in the deterioration of the nickel phosphide nanowires. |
|---|---|
| ISSN: | 2076-3417 |