| Summary: | This study investigated the influence of conventional (10 s at 1160 mW/cm<sup>2</sup>) and fast high-irradiance (3 s at 2850 mW/cm<sup>2</sup>) light curing on the micro-tensile bond strength (μTBS) of bulk-fill resin composites bonded to human dentin. Sixty-four extracted human molars were ground to dentin and randomly assigned into eight groups (n = 8 per group). After application of a three-step adhesive system (Optibond FL), four different bulk-fill composites (two sculptable and two flowable composites) were placed. Of these, one sculptable (Tetric PowerFill) and one flowable (Tetric PowerFlow) composite were specifically developed for fast high-irradiance light curing. Each composite was polymerized with the conventional or the fast high-irradiance light-curing protocol. The specimens were cut into dentin-composite sticks, μTBS was determined and failure modes were analyzed. Statistical analysis was performed using <i>t</i>-test for independent observations and one-way ANOVA. A statistical difference between the curing protocols was only found for Tetric PowerFlow, where the conventional protocol (23.8 ± 4.2 MPa) led to significantly higher values than the fast high-irradiance light-curing protocol (18.7 ± 3.7 MPa). All other composite materials showed statistically similar values for both polymerization protocols. In conclusion, the use of fast high-irradiation light curing has no negative influence on the μTBS of the investigated high-viscosity bulk-fill composites. However, it may reduce the dentin bond strength of flowable bulk-fill composite.
|
|---|