| Summary: | TCGH(TC4+GH4169)composite material was prepared by selective laser melting(SLM). The optimum forming process parameters of TCGH composite material were investigated, and the microstructure and mechanical properties of as-deposited samples and heat-treated samples were studied. The results show that the optimum process parameters for fabrication of TCGH composite material are scanning speed of 900 mm/s with laser power of 150 W, and density higher than 99.5%. The addition of GH4169 powder changes the solid phase transformation behavior of TC4 titanium alloy material, and the as-deposited structure shows obvious high temperature solidification characteristics, which makes the forming characteristics of progressive scanning overlap and layer-by-layer scanning accumulation obvious. The original coarse columnar β grain size along the printing direction is significantly reduced, and the tensile strength of the composite is improved. Compared with the as-deposited sample, the microstructure of the heat-treated sample is transformed into a near-equiaxed structure. At the same time, with the increase of heat treatment temperature, the dissolution of the second phase leads to the dominant solid solution strengthening effect of the composite material, which improves the tensile strength and plasticity of the composite material.
|
|---|