| Summary: | The effects of the metal incorporation into hydroxyapatites on the deactivation behavior of the solids were examined in the esterification of glycerol (EG) reaction. The introduction of Cu, Co, or Ni ions by ion exchange in calcium-deficient hydroxyapatites resulted in active catalysts for the EG reaction. The metal contents were varied from 2.0 to 17.0%, providing better performances at rather high metal contents. Part of metal species existed in the hydroxyapatite lattice structure and also as isolated Cu<sup>2+</sup>, Ni<sup>2+</sup>, and Co<sup>2+</sup> entities on the surface, as shown by XPS and EPR. The effects of the reaction temperature, reaction time, and glycerol to acetic acid molar ratios were deeply investigated. The spent solids used in this study were characterized by XRD, FTIR, SEM-EDS, chemical analyses, EPR, and XPS. The Cu<sup>2+</sup>–OH acid pairs could promote a superior catalytic performance of Cu-containing hydroxyapatites due to the resistance of these solids against leaching of the active species, which is even better than those of Co and Ni-containing counterparts with high metal contents. Cu into hydroxyapatite had a good reusability and long-term utilization for five consecutive cycles of 24 h under a glycerol to acetic acid molar ratio of 0.25 at 80 °C, and longer reaction times provide triacetin formation. This was due to the fact that Cu was stabilized by interacting with Ca, PO<sub>4</sub>, and OH sites into the hydroxyapatite lattice, being highly active for the EG reaction. The results also revealed that isolated Cu<sup>2+</sup> sites played an important role in enhancing the glycerol conversion, intrinsically due to the Cu-containing hydroxyapatites ability to avoid strong adsorption of glycerol oligomers on the catalytic sites.
|
|---|