Microstructure Evolution and Work Hardening Behavior of Hot-Rolled DP780 Ferrite/Bainite Dual-Phase Steel
In this article, by optimizing the alloy composition, the DP780 grade hot-rolled duplex steel was obtained by TMCP (thermo-mechanical control process) combined with medium temperature coiling procedure. The microstructure evolution and mechanical properties of the experimental steel were analyzed by...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2023-01-01
|
| Series: | Advances in Materials Science and Engineering |
| Online Access: | http://dx.doi.org/10.1155/2023/7995789 |
| _version_ | 1797846523193589760 |
|---|---|
| author | Zhengtuan Li Chunjing Wu Heli Wan |
| author_facet | Zhengtuan Li Chunjing Wu Heli Wan |
| author_sort | Zhengtuan Li |
| collection | DOAJ |
| description | In this article, by optimizing the alloy composition, the DP780 grade hot-rolled duplex steel was obtained by TMCP (thermo-mechanical control process) combined with medium temperature coiling procedure. The microstructure evolution and mechanical properties of the experimental steel were analyzed by means of optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), room temperature tensile experiment, and low-temperature impact experiment. When the coiling temperature was 540°C, the yield strength, tensile strength, and elongation of the experimental steel were 663 MPa, 785 MPa, and 23%, respectively, and the product of the strength and elongation was as high as 18.1 GPa%, which accords with the mechanical properties of the national standard for DP780 dual-phase steel. The experimental steel exhibits significant work hardening effect at higher strain, and can still guarantee a certain work hardening index and good formability. When the coiling temperature was high (570°C), the strength of the experimental steel decreased and the work hardening effect was also weakened due to the coarsening of microstructure. The results of this article provide theoretical guidance for the production of DP780 dual-phase steel by hot rolling. |
| first_indexed | 2024-04-09T17:56:21Z |
| format | Article |
| id | doaj.art-ee727ed19966403d844c21325d121f04 |
| institution | Directory Open Access Journal |
| issn | 1687-8442 |
| language | English |
| last_indexed | 2024-04-09T17:56:21Z |
| publishDate | 2023-01-01 |
| publisher | Hindawi Limited |
| record_format | Article |
| series | Advances in Materials Science and Engineering |
| spelling | doaj.art-ee727ed19966403d844c21325d121f042023-04-15T00:00:05ZengHindawi LimitedAdvances in Materials Science and Engineering1687-84422023-01-01202310.1155/2023/7995789Microstructure Evolution and Work Hardening Behavior of Hot-Rolled DP780 Ferrite/Bainite Dual-Phase SteelZhengtuan Li0Chunjing Wu1Heli Wan2School of Materials Science and EngineeringSchool of Materials Science and EngineeringHBIS Chengde Iron and Steel Group Co.In this article, by optimizing the alloy composition, the DP780 grade hot-rolled duplex steel was obtained by TMCP (thermo-mechanical control process) combined with medium temperature coiling procedure. The microstructure evolution and mechanical properties of the experimental steel were analyzed by means of optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), room temperature tensile experiment, and low-temperature impact experiment. When the coiling temperature was 540°C, the yield strength, tensile strength, and elongation of the experimental steel were 663 MPa, 785 MPa, and 23%, respectively, and the product of the strength and elongation was as high as 18.1 GPa%, which accords with the mechanical properties of the national standard for DP780 dual-phase steel. The experimental steel exhibits significant work hardening effect at higher strain, and can still guarantee a certain work hardening index and good formability. When the coiling temperature was high (570°C), the strength of the experimental steel decreased and the work hardening effect was also weakened due to the coarsening of microstructure. The results of this article provide theoretical guidance for the production of DP780 dual-phase steel by hot rolling.http://dx.doi.org/10.1155/2023/7995789 |
| spellingShingle | Zhengtuan Li Chunjing Wu Heli Wan Microstructure Evolution and Work Hardening Behavior of Hot-Rolled DP780 Ferrite/Bainite Dual-Phase Steel Advances in Materials Science and Engineering |
| title | Microstructure Evolution and Work Hardening Behavior of Hot-Rolled DP780 Ferrite/Bainite Dual-Phase Steel |
| title_full | Microstructure Evolution and Work Hardening Behavior of Hot-Rolled DP780 Ferrite/Bainite Dual-Phase Steel |
| title_fullStr | Microstructure Evolution and Work Hardening Behavior of Hot-Rolled DP780 Ferrite/Bainite Dual-Phase Steel |
| title_full_unstemmed | Microstructure Evolution and Work Hardening Behavior of Hot-Rolled DP780 Ferrite/Bainite Dual-Phase Steel |
| title_short | Microstructure Evolution and Work Hardening Behavior of Hot-Rolled DP780 Ferrite/Bainite Dual-Phase Steel |
| title_sort | microstructure evolution and work hardening behavior of hot rolled dp780 ferrite bainite dual phase steel |
| url | http://dx.doi.org/10.1155/2023/7995789 |
| work_keys_str_mv | AT zhengtuanli microstructureevolutionandworkhardeningbehaviorofhotrolleddp780ferritebainitedualphasesteel AT chunjingwu microstructureevolutionandworkhardeningbehaviorofhotrolleddp780ferritebainitedualphasesteel AT heliwan microstructureevolutionandworkhardeningbehaviorofhotrolleddp780ferritebainitedualphasesteel |